Heskins Non-Slip Fabric is a versatile and very effective anti slip mesh, useful for applying to worktops, tables, desks, inside of drawers, etc, to prevent items from slipping due to a wet surface or motion, particularly inside boat and ship cabins. The mesh has tiny air bubbles inside the foam for cushioning, helping prevent damage to delicate items, and has excellent temperature resistance.
For tool boxes and drawer insert, Heskins Black Ribbed provides deep channels for debris and dirt to fall into, and allowing moisture to drain away.
See the Heskins range of accessories for additional help during application, pro-longing the life of anti-slip tapes and line markings. The range consists of primers, edge fixing, mallets, rollers etc.
Order References
H4643 Non-Adhesive Non-Slip Fabric
Colours:
Sizes:
- 18.3m rolls with widths from 25mm up to 1300mm
H4644 Self-Adhesive Non-Slip Fabric
Colours:
Sizes:
- 18.3m rolls with widths from 25mm up to 1300mm
H4646 Thick Non-Slip Fabric
Non-adhesive, 3.7mm-thick non-slip fabric.
Colours:
Sizes:
- 15m rolls with widths from 25mm up to 1450mm
T/NET Tenura Fabric
A thicker, non-adhesive waterproof anti-slip fabric ideal for use in baths and showers.
Colours:
- Black
- White
- Red - RAL 3018
- Blue - RAL 5015
- Beige - RAL 1015
Sizes:
- 25m rolls with widths from 25mm up to 1500mm
Product Data
H4643:
This is a non-adhesive non-slip fabric.
| | Testing Methods |
---|
Overall Thickness | 0.094 | Caliper Method |
Composition | 85% PVC, 15% filament mesh | N/A |
H4644:
A self-adhesive version of H4643.
Product Composition | 85% PVC, 15% filament mesh |
Total Applied Thickness | 0.81mm |
Adhesive Construction | Pressure sensitive acrylic |
Non-Volatile, %: | 40±1 |
Viscosity @25 degree C, CPS (LVF TYPE, No. 4, 60RPM): | 3000±800 |
Solvent Composition: | ETHYL ACETATE / OTHER |
Tack (J. Dow Method) No. : | 24 |
(LOOP) KG/IN : | 1 |
Adhesion (PSTC-1, to Steel) KG / TN : | 1.5 |
(to PE): | 0.2 |
Cohesion (PSTC-7) MINS : | 4320 |
Adhesive Film Thickness, u : | 24-27 |
Substrate: | PVC |
Drying Condition: | 30 seconds at 100 degree C |
Test Condition: | 25 degree C X 70% Humidity |
H4646:
Non-adhesive, 3.7mm-thick non-slip fabric
| | Testing Methods |
---|
Overall Thickness | 3.7mm | Caliper Method |
Composition | 85% PVC, 15% filament mesh | N/A |
Tenura Fabric
Subject | Result | Test method |
---|
Back carrier | 0.65mm PVC | Caliper method |
Type of adhesive | Modified solvent acrylic | N/A |
Adhesive thickness | 0.06mm | N/A |
Total thickness | 0.71mm | N/A |
Initial tack (Kg/25.4mm) | 3.2 | PSTC-16 |
Holding power | > 24 hour | PSTC-7 |
Peel adhesion (Kg/25.4mm) | 1.4 | PSTC-1 |
Tensile strength (MD) (Kgf/cm²) | 120.4 | ASTM D882A:1997 |
Elongation | 199% | ASTM D882A:1997 |
Tear resistance (MD) (Kgf/mm) | 5.36 | ASTM D1004 : 1994-Die C |
Dimensional stability(MD) | 0% | ASTM D1593 : 1994 |
Temperature range | -30ºC to +70ºC | See notes below |
The independent test laboratory at Adhesive Technical Services Ltd performed the temperature test, England (test results available)
Coefficient of Friction Data (Tenura) |
---|
| Dry Surface Test Result | Wet Surface Test Result
|
Aqua-Safe | 106 4S | 31 4S |
The above tests were conducted on a Pendulum, the tests were conducted at a recognised independent friction testing laboratory, and copy certificates are available on request. Pendulum is a dynamic test, for static tests we also have results ASTM C 1028-96.