Carboline Thermaline 4674 is a single package medium to high temperature coating that withstands continuous temperature up to 400ºC peaks up to 540ºC. May be applied directly to properly prepared steel.
Resistant to thermal shock conditions from ambient temperature to 400ºC
Excellent weathering properties
Gloss finish
10L Aluminium also available - price on application - contact our sales team for more information on 0113 2455450 or send a message to [email protected].
Carboline Thermaline 4674 is a single package medium to high temperature coating that withstands continuous temperature up to 400ºC peaks up to 540ºC. May be applied directly to properly prepared steel. Application over inorganic zinc primers like Carbozinc 11 will provide superior performance by preventing rusting and rust streaking during a shutdown or when the equipment is exposed to moisture and/or salts at temperature less than 93ºC.
Resistant to thermal shock conditions from ambient temperature to 400ºC
Excellent weathering properties
Gloss finish
Product Specification
Technical Data
Carboline Thermaline 4674
Primer:
None required
A primer coat of Carbozinc will greatly increase performance over steel
Topcoats:
Normally none
Solid(s) Content:
By Volume 45 ± 2%
Theoretical Coverage Rate:
11,2 m²/l at 40 µm
Allow for loss in mixing and application
Dry Film Thickness:
30 - 80 microns (1.18 - 3.15 mils) per coat
Normally 40 µm. Two coats are recommended over bare steel and one or two coats over inorganic zincs such as Carbozinc 11
Excessive film thickness over inorganic zincs may result in blistering and delamination when temperature is increased.
Wet Film Thickness:
65 - 175 µm per coat, normally 90 µm
Dry Temp. Resistance:
Continuous: 400°C (752°F)
Non-Continuous: 540°C (1004°F)
Limitations:
Not recommended for linings or immersion service and exposure to splash and spillage of acids and alkalis
Shelf Life:
2 years at 24ºC
Drying Times
Curing Schedule
Surface Temp.
Between Coats
Final Cure
10°C
8 Hours
10 Hours
16°C
5 Hours
8 Hours
30°C
2 Hours
3 Hours
These times are based on 40 microns dry film thickness. Excessive film thickness or inadequate ventilation conditions after application require longer dry times and will cause premature failure in extreme cases
Final cure: To obtain optimum properties, Carboline 4674 must be cured at temperatures of 177 – 232ºC. Allow for initial increase of temperature to proceed slowly up to 177ºC over a 6 hours period
Surface Preparation
Preparation
General:
Surface must be clean and dry
Employ adequate methods to remove dirt, dust, oil and all other contaminants that could interfere with adhesion of the coating
Steel:
Abrasive blast cleaning to Sa 2½ (ISO 8501-1) is recommended with a blast profile of 25 – 40 µm
Use of thinners other than those supplied or approved by Carboline may adversely affect product performance and void product warranty, whether expressed or implied
Conventional Spray:
Pressure pot equipped with dual regulators, 3/8” I.D., minimum material hose .043” I.D. fluid tip and appropriate air cap
Airless Spray:
Pump ratio: 30 : 1 (min.)
GMP Output: 3.0 (min.)
Material Hose: 3/8” I.D. (min.)
Tip Size: .013-.015”
Output PSI: 2200
Filter Size: 60 mesh
Brush:
For small areas and touch-up only
Use a medium natural bristle brush applying full strokes, avoid re-brushing
Roller:
Application by roller is not recommended
Application Conditions
Conditions
Condition
Material
Surface
Ambient
Humidity
Minimum
4°C
4°C
4°C
0%
Maximum
38°C
54°C
54°C
95%
Industry standards are for substrate temperatures to be 3ºC above the dew point
Special application techniques may be required above or below normal application conditions
Customer agrees that before placing an Order, Customer has read and understood the most up to date Product Data Sheet for the Product. Where we have access to the Product Data Sheet from the manufacturer, we will either provide a copy on request, or include a link to the Product Data Sheet available on the manufacturer’s website. Customer further agrees that we have no liability for any errors or omissions contained within the Product Data Sheets. For more information, please see our Terms & Conditions of Sale.
Carboline Thermaline 4674 is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
Carboline Carbozinc 11 is a two-component, corrosion resistant primer that protects steel galvanically in the harshest environments.Meets Class B slip co-efficient and creep testing criteria for use on faying surfaces Rapid cure. Dry to handle in 45 minutes at 16°C and 50% relative humidity Low temperature cure down to -18°C High zinc...
These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3). Please click here for important information about these kits. Kit Contents: SET 1 (Hand Tools)1 x Rust-Oleum...