Rust-Oleum Hard Hat 2117/1017 Galva Zinc Alu
Rust-Oleum Hard Hat 2117/1017 Galva Zinc Alu is an esthetically pleasing cathodic protection for damaged galvanised steel. A fast drying, zinc rich coating based on an epoxy ester resin, this product contains pure zinc and aluminium as pigments and provides cathodic protection.
- Zinc coating with sparkling aluminium particles
- Resists 340 hours of salt spray testing (DIN 50021 SS)
- The best compromise between a zinc spray and an aluminium spray
Rust-Oleum Hard Hat 2117/1017 Galva Zinc Alu
Rust-Oleum Hard Hat Galva Zinc Alu is a fast drying, zinc rich coating based on an epoxy ester resin. The product contains pure zinc and aluminium as pigments and provides cathodic protection.
This product should be used on new, bare steel, blasted steel or galvanized steel surfaces. Primarily intended for brush application on small areas or aerosols can be used for touch-up. Can be recoated with non-saponifiable coatings. It can be used as a single coat in light industrial exposures, corrosive environments and high humidity areas.
Features & Benefits
- Sparkling aluminium finish (80% zinc, 10% alu)
- Compromise between a protection and finish
- For new, bare, rust free metal or galvanised steel
- Resists 340 hours of salt spray testing (DIN)
- Heat-resistant up to 100°C
- To handle after 3 hours (at 20°C)
- Coverage: 10.5 m²/L or 1.2m² per 500ml aerosol
RUST-OLEUM Zinc Aluminium Spray 2117 should be used on damaged galvanized steel surfaces. RUST-OLEUM Zinc Aluminium Spray 2117 is intended to be applied on small areas or for touch-up. RUST-OLEUM Zinc Aluminium Spray 2117 should be used as a single coat in light industrial exposures, corrosive environments and high humidity areas.
- Gloss Level: Matt, Metallic
- Propellant: Dimethyl ether
- Heat Resistance: 450°C (dry heat)
Drying times at 20°C/RH 50%
- Touch dry: 20 minutes
- Dry to handle: 60 minutes
- Dry to recoat: Within 2 hours or after 48 hours
- Fully cured: 7 days
Lead and chromate free thus eliminating the danger of poisonous gases escaping if the coated surface needs to be welded at a later date.
3 years from date of production in unopened cans, if stored in dry, well ventilated areas, not in direct sunlight at temperatures between 5° and 35°C.
Please contact Rawlins Paints' Technical Support Team on 0113 2455450 for more information.
It is your responsibility to read the Product Data Sheets (available below) before you place an order and prior to application of the product. The content of this website is our best recommendation and is not advice. Coverage rates quoted are approximate, you agree that coverage depends on the condition of the substrate, surface absorption, texture and application method. We ALWAYS recommend a trial area is coated to ensure the product meets your requirements before use.
- Base Type
- Based on an epoxy ester resin
- Brush, Roller, Spray
- Dry to Handle (at 20°C)
- 1 Hour
- Dry to Recoat (at 20°C)
- Within 2 hours or after 48 hours
- Fully Cured (at 20°C)
- 7 Days
- 1.2-10.4m² per litre
- Min. Application Temperature
- Heat Resistance (up-to)
- 450°C (dry heat)
- 647 g/l
- Shelf Life (from date of manufacture)
- 3 years from date of production in unopened cans, if stored in dry, well ventilated areas, not in direct sunlight at temperatures between 5° and 35°C.
- Touch Dry
- 15-20 Mins
- Recommended Dry Film Thickness
- 35 µm
- Recommended Wet Film Thickness
- 115 µm
- UN Number
- UN 1950
|mrs Ann Pearson on 26/03/2016|| |
Question: Help does this paint withstand a freezing of up to -40% only I need to paint the inside of a chest freezer which is steel but can't have any smell as store ice cream in the freezer. Thank you Ann
We would recommend you overcoat Rust-Oleum Hard Hat 2117/1017 Galva Zinc Alu with Rust-Oleum Hard Hat 2500 Transparent Protection. The application would need to take place when the freezer was out of use and at ambient temperatures. Once the coatings dry they should be fine to operate at low temperatures in a freezer.
PPG Dimetcote 9 (also known as Sigmazinc 9), is a two-component, moisture-curing zinc (ethyl) silicate coating for structural steel that can withstand substrate temperatures from –90°C (–130°F) up to 400°C (750°F), with good resistance to impact and abrasion. Anti-corrosive primer for structural steel. Specified for structural joints...
Teamac Rust Converter, is an excellent product to stop the rusting process and allow rusty surfaces to be overcoated: Easy to apply, and ideal for marine and industrial applications Can be applied to rust in existing damp conditions Suitable for rusted iron or steel Application by brush, roller or airless spray To be overcoated with a...
Tor Hi Build Zinc Phosphate Primer, a single pack high build primer for blast/manually cleaned steel. An excellent lead and chromate-free anticorrosive. Protective primer for steel A urethane alkyd binder with zinc phosphate anti-corrosive, together with inert inorganic pigments and thinned with low aromatic white spirit Good coverage -...
A corrosion resistant epoxy mastic for steel, offering very good protection against fresh and salt water. Top Features Surface tolerant Fast curing at low temperatures Good coverage
A high performance two pack epoxy solvent based surface tolerant anti-corrosive primer, specifically developed for ferrous metals which are lightly rusted. Manufactured under the auspices of an ISO 9001:2008 & ISO 14001:2004. Advantages Contains a high level of zinc phosphate anti-corrosive pigment Flexible and abrasion resistant...
Jotun Penguard HSP is a two component polyamide cured epoxy coating that is fast drying, high solids and high build. This Jotun product can be used as a primer or mid coat in atmospheric environments, specially designed for new construction where fast dry to handle and over coating times are required.
PPG SigmaCover 1500, a two-component, surface-tolerant, solvent-free, polyamine-cured epoxy primer/buildcoat for long-term protection of steel structures. Excellent corrosion resistance, with good flow and wetting properties Compatible with various aged coatings, like aged alkyd, epoxy and polyurethane Reduces explosion risk and fire...
Jotun Penguard WF is a two component, anticorrosive water borne epoxy coating that is a versatile, fast drying product containing flash rust inhibitors. It is specially designed for new construction where fast dry to handle and over coating times are required. Jotun Penguard WF can be used as primer, mid coat, finish coat or as single coat...
A high-Build zinc phosphate metal primer for new constructions and maintenance. Gives a good corrosion protection, excellent adhesion and increased application tolerance to a wide range of environmental conditions. Top Features Excellent corrosion protection Good chemical & abrasion resistance VOC compliant to current AIM regulations...
Teamac Zinc Rich Primer Aerosol, is very high concentration of metallic zinc gives cathodic protection and is a form of cold galvanising. Cold galvanises metal Protects against corrosion Use on iron Use on steel Click to jump down to Technical Data Coverage Calculator
A heavy duty, high build coating for protection of steel in corrosive environments. Gives a hard and smooth surface with excellent flexibility. Top Features Excellent immersion performance in water. Suitable as a rust preventing coating in ballast tanks. Ideal for areas prone to condensation. Very good abrasion resistance.
This epoxy is a fast-curing, heavy-duty, high-build anti-corrosive coating with a broad and versatile list of uses in marine and other corrosive environments. It is an excellent choice for the protection of ship hull exteriors, underwater and ballast tanks. Top Features Excellent immersion performance in water Suitable as a rust...
A high solids corrosion resistant primer or intermediate coat on concrete, steel and (in)organic zinc primers. Top Features Excellent corrosion protection. Excellent film build and edge protection. VOC compliant to current AIM regulations.
PPG SigmaWeld 199 is a two-component, moisture-curing low zinc (ethyl) silicate prefabrication primer that is suitable for automatic application on shot blasted steel plates. Good cutting and excellent welding properties, including MIG/MAG welding in various positions (either automatic or manual welding), fast-drying and low fume release are...
HMG Polykote HS Rapidbuild 2K Primer is a high quality 2K Isocyanate cured Acrylic Polyurethane Primer/Filler. Fast drying Easy to sand Can be used as a surfacer when applied as a thin coat on previously primed or painted substrates. Click to jump down to Technical Data