Sherwin-Williams Macropoxy M905
M905
Sherwin-Williams Macropoxy M905 (formerly known as Epigrip M905) is a low temperature curing, two pack epoxy high build undercoat, capable of curing down to 0°C.
Sherwin-Williams Macropoxy M905 (formerly known as Epigrip M905) is a low temperature curing, two pack epoxy high build undercoat, capable of curing down to 0°C.
Macropoxy M905 is used for application onto suitably primed surfaces, as an undercoat for use under suitable high performance finishes, where low temperature curing is required. It is also recommended for rapid overcoating and faster handling times.
Endorsements
Highways Agency Item No. 116
Network Rail Item Nos 7.1.7 and 7.2.2
Recommended Primers
Compatible with a wide range of epoxy primers, whereby Macropoxy M902 Winterfast Hi-Build Brushing Aluminium is the preferred primer.
Recommended Topcoats
For overcoating with epoxy products (including self overcoating), the maximum recommended interval is 28 days at 23°C. For overcoating outside this interval, consult Sherwin-Williams technical support for advice.
Where a high degree of gloss and colour retention is required overcoat with Acrolon C137V2, Acrolon C237, Acrolon 1850 and Acrolon 7300 within 7 days at a minimum dft of 50 microns or in the case of Acrolon C750V2 overcoat within 4 days. These overcoating times refer to achievement of optimum adhesion at 23°C and will vary with temperature.
For overcoating with alkyd systems consult Technical Team for advice.
Application Conditions & Overcoating
In conditions of high relative humidity, ie 80-85% good ventilation conditions are essential. Substrate temperature shall be at least 3°C above the dew point and always above 0°C.
Application at ambient air temperatures below 5°C is not recommended where there is a risk of ice formation on the substrate.
Due to the high solids content of this material, it is not normally possible to achieve at dry film thicknesses much less than 100 microns by brush application. Development of satisfactory physical properties including hardness and abrasion resistance will be obtained within 24-48 hours at a temperature of 5°C. Optimum water and chemical resistance will be achieved when the material is fully cured.
If it is desired to overcoat outside the times stated on the data sheet, please seek advice of Technical Team.
It is your responsibility to read the Product Data Sheets (available below) before you place an order and prior to application of the product. The content of this website is our best recommendation and is not advice. Coverage rates quoted are approximate, you agree that coverage depends on the condition of the substrate, surface absorption, texture and application method. We ALWAYS recommend a trial area is coated to ensure the product meets your requirements before use.
Customer agrees that before placing an Order, Customer has read and understood the most up to date Product Data Sheet for the Product. Where we have access to the Product Data Sheet from the manufacturer, we will either provide a copy on request, or include a link to the Product Data Sheet available on the manufacturer’s website. Customer further agrees that we have no liability for any errors or omissions contained within the Product Data Sheets. For more information, please see our Terms & Conditions of Sale.
Macropoxy 400 (formerly known as Sherwin-Williams Macropoxy C400V3) multi-functional epoxy zinc phosphate coating is suitable for the protection of steelwork in a range of exposure environments from C1 to C5. It was recently used on The Shard for corrosion protection.
Recommended Uses
Buildings
Car parks
Petrochemical plants
Breweries...
Nu-Steel SP Anti Corrosive Primer/Undercoat is a high performance phosphate primer that is perfect for external metal structures that are exposed to the elements.
Advantages
High performance primer and undercoat.
First class adhesion.
8-10m²/Litre average.
12-month shelf life.
Sherwin-Williams Macropoxy L425 is a two-pack epoxy zinc phosphate primer to use as anti-corrosive protection of carbon steel surfaces prepared by abrasive blast cleaning.
Recommended Systems
Macropoxy
Dura-plate
Zinc Clad Epoxy Primers
Zinc Clad Epoxy Buildcoats
A fast drying modified alkyd anti-corrosive primer for use as a general-use fast drying prefabrication or system primer on properly prepared ferrous surfaces. Manufactured under the auspices of an ISO 9001:2008 & ISO 14001:2004
Advantages
Protects against corrosion on properly prepared steel
Pigmented with zinc phosphate
Touch dry in as little as an...
This epoxy is a fast-curing, heavy-duty, high-build anti-corrosive coating with a broad and versatile list of uses in marine and other corrosive environments. It is an excellent choice for the protection of ship hull exteriors, underwater and ballast tanks.
Top Features
Excellent immersion performance in water
Suitable as a rust...
A heavy-duty primer formulated to provide long term protection of structural steel. It provides excellent adhesion and can be welded through to yield sound welds.
Top Features
Good for extended exposure demands
Ability to be welded through
Heavy-metal free
Rust-Oleum Hard Hat 2185/1085 Galva Zinc is the No.1 high zinc content coating providing superior protection and durability for metals exposed to the elements or adverse artificial conditions. Can be used as a primer or as a single coat in light industrial exposures, corrosive environments and high humidity areas. 90% zinc content, touch dry...
International Interzinc 52 is a two component, metallic zinc rich epoxy primer which complies with the composition and performance requirements of SSPC Paint 20. It has been designed to provide excellent corrosion resistance in both maintenance and new construction situations.
A high solids corrosion resistant primer or intermediate coat on concrete, steel and (in)organic zinc primers.
Top Features
Excellent corrosion protection.
Excellent film build and edge protection.
VOC compliant to current AIM regulations.
A fast drying, water based, anti-corrosive primer for temporary metal protection intended as the first coat in shop coating applications and provides the required basic protection following metal fabrication and assembly operations.
Sherwin-Williams Macropoxy C425V2 (formerly Epigrip C425V2) is a high build 2-pack epoxy zinc phosphate primer/buildcoat to provide anti-corrosive protection of carbon steel surfaces prepared by abrasive blast cleaning. Network Rail and NORSOK approved, ideal for use in internal/external exposed conditions including offshore, petrochemical and sub-sea...
A low temperature and rapid curing primer/finish with an extended recoat window that provides excellent corrosion resistance as a primer, intermediate or finish coat on to steel.
Top Features
Low-temperature characteristics
Rapid handling
Low yellowing
VOC compliant
Nullifire PM019 Primer for Blasted Steel Substrates is an anti-corrosive transport primer for temporary protection of blasted steel substrates, which will be finished with a compatible basecoat. Applied at standard film thickness, the protection in outdoor conditions is limited to approximately 3 months. Within this period of time the finishing coating...
International Interplate 855 is a fast drying, two component, weldable zinc silicate pre-fabrication primer for application by manual or automatic spray used as a temporary protective primer for the coating of steelwork prior to the fabrication process.
Cromadex 902 One Pack Etch Primer is a one pack etch primer that can be both air dried and stoved making it suitable for use in most paint shops. The product has enhanced adhesion properties to mild steel ensuring the success of the coating system. Cromadex 902 is available in white, grey and black.