We no longer stock this product, but can recommend Tikkurila Temabond ST 200 as a great alternative.

Bradite Surface Tolerant Primer is a high performance epoxy solvent-based surface tolerant anti-corrosive primer capable of being applied over lightly rusted ferrous surfaces, such as:

• Fences
• Gates
• Lightly-rusted Shipping containers
• Factory

Ideally suited for surfaces and structures on which thorough blast cleaning may not be feasible or practical.

Manufactured under the auspices of an ISO 9001:2008 quality & ISO 14001:2004 environmental management systems. 2004/42/EC EU limit value for this product (cat.A/j sb): 500g/l (2010). This product contains max. 373 g/l VOC.

Features & Benefits

• Polymide adduct cured primer for steel.
• Contains a high level of zinc phosphate anti-corrosive pigment.
• Forms a tough and hard-wearing film.
• Flexible and abrasion resistant.
• Will cure in low temperatures, even down to 0°C.
• Conforms with parts CP5C of BS5493.
• Two-pack epoxy system.
• Eggshell sheen.

Preparation

Industrial protective coating

High pressure steam cleaning to remove all loose, flaking paint and contamination back to a sound surface. Bradite TD39 industrial strength detergent, washing and rinsing should be used with scrubbing to remove grease or oil.

For new or total repair, steel should be blast cleaned to SIS Sa 21/2 minimum with a blast profile of 35-50 microns. (For maintenance repair, sweep blast or mechanically abrade existing coating to provide a key. Damaged or rusty areas should be blast cleaned to SIS Sa 21/2 or mechanically abraded to SIS St 3 minimum).

1st coat: Bradite Surface Tolerant Epoxy Primer EP92.

2nd coat: Bradite HB MIO Epoxy Build Finish EM97.

3rd coat: Bradite Polyurethane Gloss Finish PG77.

4th coat: Bradite Polyurethane Gloss Finish PG77.

Wet blasted steel

High pressure steam cleaning to remove all loose, flaking paint and contamination back to a sound surface. Bradite TD39 industrial strength detergent, washing and rinsing should be used with scrubbing to remove grease or oil.

Steel should be wet blast cleaned to SIS Sa 21/2 minimum with a blast profile of 35-50 microns then rinsed with fresh water, with excess water being blown off with oil free compressed air. (For maintenance repair, wet blast as previous, feather existing coating to a sound edge and abrade to provide a key.)

1st coat: Bradite Surface Tolerant Epoxy Primer EP92.

2nd coat: Bradite HB MIO Epoxy Build Finish EM97.

3rd coat: Bradite Polyurethane Gloss Finish PG77.

In all cases, an induction period of 20 minutes after mixing is required if material temperatures are below 10oC. For maintenance painting, the 1st coat will be a touch up to bare areas only.

Application

Application and use should always conform to the codes of practice described in BS 6150 and BS 5493.

Brush and Roller: supplied ready for use. Thin, if required, with 0-10% Bradite Thinner TE36.

Conventional Air Spraying: Thin with 10-20% Bradite Thinner TE36 as required, tip size - 3.0mm, tip pressure 60psi (0.4MPa) approximately.

Airless Spraying: Thin with 0-15% Bradite Thinner TE36 as required, tip size - 19 thou (0.48mm) approximately, tip pressure - 2100 psi (15MPa) approximately.

Clean all equipment immediately after use with Bradite Thinner TE36 for best results. Always refer to the Health and Safety sheet for the product before use, and observe the warning phrases on the label.