Bradite CR Anti-Corrosive Primer
Bradite CR Anti-Corrosive Primer is a high performance single pack chlorinated rubber anti-corrosive primer with excellent chemical & water resistance. Dries quick and for application on to suitably prepared ferrous metals. Manufactured under the auspices of an ISO 9001:2008 & ISO 14001:2004.
- Contains zinc phosphate
- Excellent acid and alkali chemical resistance
- Can be used at low temperatures, even as low as 0°C
Please note: Colours are sold in the nearest tin size but actual paint volume per tin may vary up to 10% depending on colour.
**Available for delivery - see Delivery Options below**
Product customisationDon't forget to save your customization to be able to add to cart
Bradite CR Anti-Corrosive Primer is a high performance single pack chlorinated rubber anti-corrosive primer with excellent chemical & water resistance. A quick drying primer, for use on suitably prepared ferrous surfaces such as fences, gates, shipping containers, etc.
Additionally, this primer may be used to prime ferrous metalwork within factories, industrial outlets and production plants, such as: automotive production lines, industrial laundry and commercial sewing factory.
Manufactured under the auspices of an ISO 9001:2008 quality & ISO 14001:2004 environmental management systems.
Features & Benefits
- Contains zinc phosphate, to protect against corrosion.
- Can be used as a priming coat in a protective paint system, to give good anti-corrosive properties.
- Excellent acid and alkali chemical resistance.
- Can be used at low temperatures, even as low as 0°C.
- Eggshell sheen.
Substrate should be dust free and completely dry before coating.
High pressure water cleaning to remove all loose and flaking paint and contamination back to a sound substrate. For best performance, complete vacuum blast cleaning of the substrate is recommended. Bradite TD39 industrial strength detergent washing and rinsing should be used with scrubbing to remove grease or oil.
Intact areas of existing coatings should be roughened by abrasive manual or disc rubbing and feathered back to a sound coating edge. Cracks and pits should be filled using a suitable screed or mortar before painting.
Steel should be blast cleaned to SIS-Sa 2½ minimum, blast profile 35-50 microns and surface free of soluble salts, or de-rusted manually or mechanically to SIS-St 3 minimum.
Painting System - Industrial New Build & Maintenance
1st coat: Bradite Chlorinated Rubber Eggshell CP26.
2nd coat: Bradite Chlorinated Rubber Eggshell CC24.
3rd coat: Bradite Chlorinated Rubber Eggshell CC24 - for a gloss finish, substitute final coat with Bradite Chlorinated Rubber Gloss CG23.
For galvanised steel and other non-ferrous surfaces, the first coat should be substituted with Bradite Barrier Primer EU96. For maintenance, the first coat will be spot priming exposed substrate only.
Application and use should always conform to the codes of practice described in BS 6150 and BS 5493
Brush and Roller: Thin with 0-5% Bradite Thinner TC32 as required.
Conventional Air Spraying: Thin with 10-20% Bradite Thinner TC32 as required, tip size – 2.0 mm, tip pressure 60psi (0.4MPa) approximately.
Airless Spraying: Thin with 5-10% Bradite Thinner TC32 as required, tip size - 23 thou (0.58mm) approximately, tip pressure - 2100 psi (15MPa) approximately.
Clean all equipment immediately after use with Bradite thinner TC32 for best results. Always refer to the Health and Safety sheet for the product before use, and observe the warning phrases on the label.
- Water / Solvent Based
- For Use On
- Ferrous Metals
- Application Method
- Conventional Air Spray, Airless Spray, Brush, Roller
- Standard / Ready Mixed
- Single, Two or Three Pack
- Product Certifications
- ISO 9001:2008, ISO 14001:2004 environmental management systems
- Pack Size
- 10m2 per Litre
- Touch Dry
- 30 Mins
- UN Number
Be the first to ask a question about this product!