Tikkurila Temacoat SPA 50 is a two-component resin modified epoxy paint that can be applied to steel, zinc and aluminium as an excellent primer, intermediate or finish coat on surfaces exposed to stress and is also suitable as a single-coat system.

Recommended for building frameworks, tubular bridges, conveyors and other steelwork and equipment

Forms durable film with good mechanical, chemical and climatic resistant properties

For industrial and professional use only.

Quick Links - Click To Jump To Section:

• Features & Benefits
• Technical Data
• Surface Preparation
• Recommended Primers
• Recommended Topcoats
• Application Conditions
• Mixing Components
• Application
• Thinners & Cleaners

Features & Benefits

• Can be applied to steel, zinc and aluminium
• Rapidly recoatable and ready to handle paint
• It is also suitable as a single-coat system
• Forms durable film with good mechanical, chemical and climatic resistant properties
• Excellent as a primer, intermediate or finish coat on surfaces exposed to stress
• Recommended for building frameworks, tubular bridges, conveyors and other steelwork and equipment

Technical Data

• Volume Solids: 68±2% (ISO 3233)
• Weight Solids: 81±2%
• Specific Gravity: 1.4–1.5 kg / l (mixed)
• VOC:
• The Volatile Organic Compounds amount is 300 g/litre of paint mixture.
• VOC content of the paint mixture (thinned 10% by volume) is 360 g/l.
• Mixing Ratio:
• Base 4 parts by volume Temacoat SPA 50
• Hardener 1 part by volume 008 5607
• Pot Life (at 23℃)
• 6 hours

Recommended Film Thicknesses and Theoretical Coverage

Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.

Drying Times

Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.

Surface Preparation

Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces:

• Blast clean to grade Sa2½. (ISO 8501-1)
• If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.

Zinc surfaces:

• Sweep blast clean with mineral abrasives, e.g. quartz sand, to an even roughness. (SaS, SFS 5873)
• If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with Panssaripesu detergent.
• For hot dip galvanized surfaces see separate application instructions or contact Tikkurila Technical Service/Rawlins Technical on 0113 2455450 (option 2) or send a message to [email protected]

Aluminium surfaces:

• Sweep blast clean with non-metallic abrasives to an even roughness. (SaS, SFS 5873)
• If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with Maalipesu detergent.

Primed surfaces:

• Oil, grease, salt and dirt are removed from the surface by appropriate means.
• Repair any damage to the primer coat.
• Note the overcoating time of primer. (ISO 12944-4)

Recommended Primers

• Temacoat SPA Primer
• Temazinc 77
• Temazinc 99

Recommended Topcoats

• Temacoat GPL
• Temacoat GS 50
• Temacoat GPL-S MIO
• Temacoat SPA 50
• Temadur 10
• Temadur 20
• Temadur 50
• Temadur 90
• Temadur HS 90
• Temadur SCF 20
• Temadur SC-F 50
• Temadur SC-F 80
• Temathane 50
• Temathane 90
• Temathane PC 50
• Temathane PC 80

Application Conditions

• All surfaces must be clean, dry and free from contamination.
• During application and drying the temperature of the surface should not fall below 0°C.
• The surface temperature of steel should remain at least 3°C above the dew point.
• Relative humidity of the air should not exceed 80% during application and drying.
• For proper application the temperature of the product itself should be above +15°C during mixing and application.
• The product should not be applied at temperatures below 0°C when there is a possibility of ice formation on the substrate.
• For proper application the temperature of the product itself should be above +15°C during mixing and application.
• Good ventilation and sufficient air movement is required in confined areas during application and drying.

Note! There is a natural tendency of this coating to chalk, discolor or yellow unevenly. It is recommended to use polyurethane topcoat when there are high aesthetical requirements on colour appearance.

Mixing Components

• First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use.
• Use power mixer for mixing.
• Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface and weaken the properties of the coating.

Application

• For airless spraying, the product is thinned approximately 0–10%.
• Recommended nozzle tip is 0.015"–0.021" and pressure 120–180 bar.
• Spray angle shall be chosen according to the shape of the object.
• For brush application product should be thinned according to the circumstances.

Thinners & Cleaners

• Thinner 1031