Tikkurila Temacoat SPA Primer, a two-component resin modified epoxy primer with anti-corrosive pigments with excellent adhesion to steel, zinc and aluminium surfaces, that can be applied in thick layers, thus enabling faster production.
Has high solids content
Used as a primer or an intermediate coat in paint systems exposed to abrasion and chemical stress
Pigmented with zinc phosphate
Recommended for building frameworks, tubular bridges, conveyors and other steelwork and equipment
Product customisation
Don't forget to save your customization to be able to add to cart
Tikkurila Temacoat SPA Primer is a two-component resin modified epoxy primer with anti-corrosive pigments with excellent adhesion to steel, zinc and aluminium surfaces. It can be applied in thick layers, thus enabling faster production.
Used as a primer or an intermediate coat in paint systems exposed to abrasion and chemical stress; recommended for building frameworks, tubular bridges, conveyors and other steelwork and equipment.
Has high solids content and can be applied in thick layers, thus enabling faster production
Used as a primer or an intermediate coat in paint systems exposed to abrasion and chemical stress
The paint adheres well to steel, zinc and aluminium surfaces
Pigmented with zinc phosphate
Recommended for building frameworks, tubular bridges, conveyors and other steelwork and equipment
Technical Data
Volume Solids: 67±2%(ISO 3233)
Weight Solids: 80±2%
Specific Gravity: 1.4 kg / l (mixed)
VOC:
The Volatile Organic Compounds amount is 300 g/litre of paint mixture.
VOC content of the paint mixture (thinned 10% by volume) is 360 g/l.
Mixing Ratio:
Base 4 parts by volume Temacoat SPA Primer
Hardener 1 part by volume 008 5607
Pot Life (at 23℃)
6 hours
Recommended Film Thicknesses and Theoretical Coverage
Recommended film thicknesses
Theoretical coverage
Wet
Dry
120µm
80µm
8.4 m²/l
225µm
150µm
4.4 m²/l
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Drying Times
DFT 100 µm
0°C
10°C
23°C
35°C
Dust dry, after
16h
4h
2h
1h
Touch dry, after
24h
10h
4h
2h
Recoatable, min. after
24h
3h
1h
½h
Recoatable, surfaces to be submerged, min. after
4d
28h
12h
6h
Recoatable with polyurethane paints, min. after
1d
5h
2h
1h
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Surface Preparation
Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)
Steel surfaces:
Blast clean to grade Sa2½. (ISO 8501-1)
If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.
Zinc surfaces:
Sweep blast clean with mineral abrasives, e.g. quartz sand, to an even roughness. (SaS, SFS 5873)
If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with Panssaripesu detergent.
For hot dip galvanized surfaces see separate application instructions or contact Tikkurila Technical Service/Rawlins Technical on 0113 2455450 (option 2) or send a message to [email protected]
Aluminium surfaces:
Sweep blast clean with non-metallic abrasives to an even roughness. (SaS, SFS 5873)
If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with Maalipesu detergent.
Primed surfaces:
Oil, grease, salt and dirt are removed from the surface by appropriate means.
Repair any damage to the primer coat.
Note the overcoating time of primer. (ISO 12944-4)
All surfaces must be clean, dry and free from contamination.
During application and drying the temperature of the surface should not fall below 0°C.
The surface temperature of steel should remain at least 3°C above the dew point.
Relative humidity of the air should not exceed 80% during application and drying.
For proper application the temperature of the product itself should be above +15°C during mixing and application.
The product should not be applied at temperatures below 0°C when there is a possibility of ice formation on the substrate.
For proper application the temperature of the product itself should be above +15°C during mixing and application.
Good ventilation and sufficient air movement is required in confined areas during application and drying.
Note! There is a natural tendency of this coating to chalk, discolour or yellow unevenly. It is recommended to use polyurethane topcoat when there are high aesthetical requirements on colour appearance.
Mixing Components
First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use.
Use power mixer for mixing.
Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface and weaken the properties of the coating.
Application
For airless spraying, the product is thinned approximately 0–10%.
Recommended nozzle tip is 0.015"–0.021" and pressure 120–180 bar.
Spray angle shall be chosen according to the shape of the object.
For brush application product should be thinned according to the circumstances.
Customer agrees that before placing an Order, Customer has read and understood the most up to date Product Data Sheet for the Product. Where we have access to the Product Data Sheet from the manufacturer, we will either provide a copy on request, or include a link to the Product Data Sheet available on the manufacturer’s website. Customer further agrees that we have no liability for any errors or omissions contained within the Product Data Sheets. For more information, please see our Terms & Conditions of Sale.
Tikkurila Temacoat GPL-S MIO is a two-component, polyamide cured epoxy paint pigmented with micaceous iron oxide, with superior adhesion to steel surfaces forming a very strong and durable film that can be used as a primer or an intermediate coat in aggressive environments
Fast cure and low-temperature cure hardeners available - click to...
Temacoat GPL, a two-component, amine adduct cured mar and chemical resistant epoxy topcoat used especially as a finishing coat especially for objects exposed to heavy abrasion and chemical attack. Due to CE marking it is also suitable for concrete surfaces in process industries.
Recommended for bridges, tanks and different types of...
Tikkurila Temacoat GS 50, a two-component, polyamide-cured high build epoxy finishing and intermediate coat for protection of steel framework, conveyors, tubular bridges and other steel structures from abrasion and mechanical and/or chemical stress.
Fast cure hardener available on request
Can also be used as a sealer or a single-coat paint...
Tikkurila Temacoat SPA 50 is a two-component resin modified epoxy paint that can be applied to steel, zinc and aluminium as an excellent primer, intermediate or finish coat on surfaces exposed to stress and is also suitable as a single-coat system.
Rapidly recoatable and ready to handle paint
Forms durable film with good mechanical,...
Tikkurila Temadur 50, a time-proven, easy-to-use general purpose topcoat for constructional steelwork and machinery, with a wide range of colours to choose from.
Two-component, durable and non-chalking semi-gloss polyurethane paint, hardener aliphatic isocyanate
Forms a durable, easy-to-clean and non-chalking topcoat with good gloss and...
Tikkurila Temadur 90, 2-pack, high gloss polyurethane paint recommended to be used as a glossy decorative finishing coat for epoxy systems on a variety of substrates such as steel, aluminium, concrete etc. exposed to severe weathering and/or chemical stress.
Forms a durable, easy-to-clean and non-chalking topcoat with outstanding gloss and...
Tikkurila Temazinc 99, a 2-component, polyamide cured zinc-rich epoxy paint providing superior cathodic protection for steel, used as a primer in epoxy, polyurethane, acrylic and chlorinated rubber systems for steel surfaces exposed to severe climatic conditions.
Prequalified in the NORSOK system 1; an excellent choice for the most...
Tikkurila Temazinc 77, a primer with good cathodic protection for steel containing over 80% zinc, fully meeting requirements of the standard ISO 1294-5 for zinc-rich primers.
Used in coating systems where extended durability is required
Used as a primer in epoxy, polyurethane, acrylic and chlorinated rubber systems for steel surfaces...
Tikkurila Temathane PC 50, a high-solids two-component, semi-gloss polyurethane paint, hardener aliphatic isocyanate recommended for painting of storage tank exteriors, steel buildings and other steelwork.
Huge colour range available, with RAL, BS & NCS shades
Prequalified in the NORSOK system 1 and therefore an excellent choice for...
Tikkurila Temathane PC 80, a high-solids two-component, glossy polyurethane paint (with hardener aliphatic isocyanate) that is particularly suitable for harsh environments, helping extend the service life of the paint system.
Huge colour range with RAL, BS & NCS shades
Excellent choice when a high-solids topcoat with extremely good...
Tikkurila Temathane 50 is a two-component, semi-gloss polyurethane paint, hardener aliphatic isocyanate.
Dries rapidly and is easy to apply.
Recommended to be used as a semi-gloss topcoat for epoxy and polyurethane systems exposed to weathering.
A durable, easy to clean and non-chalking topcoat.
Excellent weathering and abrasion...
These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3).
Please click here for important information about these kits.
Kit Contents:
SET 1 (Hand Tools)
1 x Rust-Oleum...