Bradite HB MIO Build Coat
  • Bradite HB MIO Build Coat

Bradite HB MIO Build Coat

EM97

Bradite HB MIO Build Coat is a high performance two pack epoxy solvent-based micaceous iron oxide coating and finish for use as an intermediate build coat or finish on suitably primed steel and non-ferrous substrates. Manufactured under the auspices of an ISO 9001:2008 & ISO 14001:2004

Advantages

  • Recoatable after long periods of exposure
  • Conforms with parts KU1 C/D and KF 1 E/F of BS5493
  • Ideal for marine environments

Colour
  • Current colour: Bradite Black
Choose a colour
Close colour picker
  • RAL9007 - Grey Aluminium
  • Bradite Black
  • Bradite Blue
  • Bradite Brown
  • Bradite BS-00-A-05
  • Bradite BS-12-B-21
  • Bradite Gold
  • Bradite Green
  • Bradite Mauve
  • Bradite Medium Grey
  • Bradite Natural
  • Bradite Red
  • Bradite Silver
Size
Finish
£64.65
VAT excluded

£77.58 Tax incl.
Quantity

Description

Bradite HB MIO Build Coat is a high performance epoxy coating and finish for use as an intermediate build coat or finish on suitably primed steel and non-ferrous substrates. Producing a tough, hard wearing coating that is recoatable even after long periods of exposure.

The two-pack coating is a solvent-based solution and has excellent anti-corrosive performance in industrial and marine environments.

Manufactured under the auspices of an ISO 9001:2008 quality & ISO 14001:2004 environmental management systems. 2004/42/EC EU limit value for this product (cat.A/j sb): 500g/l (2010). This product contains max. 375 g/l VOC.


Features & Benefits

  • High build epoxy coating.
  • Conforms with parts KU1 C/D and KF 1 E/F of BS5493.
  • Recoatable after long periods of exposure.
  • Excellent anti-corrosive performance in industrial and marine environments.
  • Eggshell finish.
  • Touch dry in 2 hours.


Preparation

Industrial protective coating

High pressure steam cleaning to remove all loose, flaking paint and contamination back to a sound surface. Bradite TD39 industrial strength detergent, washing and rinsing should be used with scrubbing to remove grease or oil.

For new or total repair, steel should be blast cleaned to SIS Sa 21/2 minimum with a blast profile of 35-50 microns. (For maintenance repair, sweep blast or mechanically abrade existing coating to provide a key. Damaged or rusty areas should be blast cleaned to SIS Sa 21/2 or mechanically to SIS St 3 minimum).

1st coat: Bradite Surface Tolerant Epoxy Primer EP92 (substitute with Bradite Barrier Primer EU96 on galvanised metal, aluminium and other non-ferrous metal surfaces).

2nd coat: Bradite HB MIO Epoxy Build Finish EM97.

3rd coat: Bradite Polyurethane Gloss Finish PG77.

4th coat: Bradite Polyurethane Gloss Finish PG77.

Wet blasted steel

High pressure steam cleaning to remove all loose, flaking paint and contamination back to a sound surface. Bradite TD39 industrial strength detergent, washing and rinsing should be used with scrubbing to remove grease or oil.

Steel should be wet blast cleaned to SIS Sa 2 1/2 minimum with a blast profile of 35-50 microns then rinsed with fresh water, with excess water being blown off with oil free compressed air. For maintenance repair, wet blast as previous, feather existing coating to a sound edge and abrade to provide a key.

1st coat: Bradite Surface Tolerant Epoxy Primer EP92.

2nd coat: Bradite HB MIO Epoxy Build Finish EM97.

3rd coat: Bradite Polyurethane Gloss Finish PG77.


Preparation

High temperature applications (200°C)

High pressure steam cleaning to remove all loose, flaking paint and contamination back to a sound surface. Bradite TD39 industrial strength detergent, washing and rinsing should be used with scrubbing to remove grease or oil.

For new or total repair, steel should be blast cleaned to SIS Sa 21/2 minimum with a blast profile of 35-50 microns. For maintenance repair, sweep blast or mechanically abrade existing coating to provide a key. Damaged or rusty areas should be blast cleaned to SIS Sa 21/2 or mechanically to SIS St 3 minimum.

1st coat: Bradite HB MIO Epoxy Build Finish EM97.

2nd coat: Bradite HB MIO Epoxy Build Finish EM97.

3rd coat: Bradite HB MIO Epoxy Build Finish EM97.

In all cases, an induction period of 20 minutes after mixing is required if material temperatures are below 10°C. 


Application

Application and use should always conform to the codes of practice described in BS 6150 and BS 5493. 

Brush and Roller: Supplied ready for use. Thin, if required, with 0-10% Bradite Thinner TE36.

Conventional Air Spraying: Thin with 10-20% Bradite Thinner TE36 as required, tip size - 3.0mm, tip pressure 60psi (0.4MPa) approximately.

Airless Spraying: Thin with 0-15% Bradite Thinner TE36 as required, tip size - 19 thou (0.48mm) approximately, tip pressure - 2100 psi (15MPa) approximately. Cleaning Clean all equipment immediately after use with Bradite Thinner TE36 for best results. 

Clean all equipment immediately after use with Bradite Thinner TE36 for best results. Always refer to the Health and Safety sheet for the product before use, and observe the warning phrases on the label.

Product Details
EM97

Data sheet

For Use On
Steel
Application Method
Brush, Roller, Spray
Sheen
Eggshell
Colour
Standard / Ready Mixed
Single, Two or Three Pack
Single
Pack Size
5L
Application
Brush, Roller, Spray
Coverage
7.5m2 per Litre
Touch Dry
2 Hours
UN Number
UN1263
Attachments
Download


Customer agrees that before placing an Order, Customer has read and understood the most up to date Product Data Sheet for the Product. Where we have access to the Product Data Sheet from the manufacturer, we will either provide a copy on request, or include a link to the Product Data Sheet available on the manufacturer’s website. Customer further agrees that we have no liability for any errors or omissions contained within the Product Data Sheets. For more information, please see our Terms & Conditions of Sale.