Bradite HB MIO Coat/Finish
Bradite HB MIO Coat/Finish is a high build high performance single pack modified alkyd micaceous iron oxide intermediate coat. Gives excellent decorative anti-corrosive properties when used as a coating or finish in a conventional paint system. Conforms to MOD TS10201 specification & BS5493 parts FU2C/FF3D.
- Good toughness and abrasion resistance
- Good UV resistance
- British gas reference BGC BU2, BU3, BU4
- See further below for colour swatches available
**Available for delivery - see Delivery Options below**
Bradite HB MIO Coat/Finish is a high performance single pack modified alkyd micaceous iron oxide intermediate coat/finish. Perfect for the protection and decoration of ferrous & non-ferrous metals, either as an intermediate build coat or finish.
The high build coating gives excellent anti-corrosive properties when used as a coating or finish in a conventional paint system. The Bradite HB MIO Coat/Finish is available in assortment of colours - for times when decoration is just as important as protection.
Manufactured under the auspices of an ISO 9001:2008 quality & ISO 14001:2004 environmental management systems.
Features & Benefits
- Good toughness and abrasion resistance.
- Good UV resistance.
- Conforms to MOD TS10201 specification & BS5493 parts FU2C/FF3D.
- British gas reference BGC BU2, BU3, BU4.
- Eggshell sheen level.
High pressure steam cleaning to remove all loose, flaking paint and contamination back to a sound surface. Bradite TD39 industrial strength detergent, washing and rinsing should be used with scrubbing to remove grease or oil.
Remove all rust scale, loose mill scale or other corrosion products by scraping and mechanical cleaning to SIS-St 3 (ISO 8501-1:1998).
Intact areas of existing coatings should be roughened by abrasive manual or disc sanding, feathering back to a sound coating edge. Cracks and pits should be filled using a suitable metal filler before painting. Substrate should be dust free and completely dry before coating.
Light surface rusting may be effectively treated using one coat of Bradite Rust Converter RC46 prior to application of this product.
New galvanised steel should be thoroughly degreased and then pre-treated with Bradite Mordent Solution TM38 prior to application of this product. Alternatively, or for other non-ferrous metals, prime with Bradite Barrier Primer EU96 before application of this product.
For the protection of metal structures subject to more demanding exposure scenarios, application of Fastrac Antico Primer AP71 or SORTED WP45, prior to finishing with this product, is highly recommended.
Application and use should always conform to the codes of practice described in BS 6150 and BS 5493. Best results are obtained by spraying.
Brush and Roller: Supplied ready for use. Use natural bristle brush, tapered and flagged, for best appearance. Thin, if required, with 0-5% Bradite Thinner TW35. Keep application in one direction to avoid “suede” like appearance & colour discontinuity.
Conventional Air Spraying: Thin with 5-15% Bradite Thinner TW35 as required, tip size – 3 mm, tip pressure 60psi (0.4MPa) approximately.
Airless Spraying: Thin with 0-10% Bradite Thinner TW35 as required, tip size - 18 thou (0.46mm) approximately, tip pressure - 2100 psi (15MPa) approximately.
Clean all equipment immediately after use with Bradite Thinner TW35 for best results. Always refer to the Health and Safety sheet for the product before use, and observe the warning phrases on the label.
- For Use On
- Ferrous Metals, Non-Ferrous Metals
- Application Method
- Brush, Roller, Spray
- Standard / Ready Mixed
- Single, Two or Three Pack
- Pack Size
- Brush, Roller, Spray
- 12m2 per Litre
- Touch Dry
- 4 Hours
Be the first to ask a question about this product!