Temacoat GPL, a two-component, amine adduct cured mar and chemical resistant epoxy topcoat used especially as a finishing coat especially for objects exposed to heavy abrasion and chemical attack. Due to CE marking it is also suitable for concrete surfaces in process industries.
Recommended for bridges, tanks and different types of steelwork and equipment in the wood processing and chemical industries, such as tubular bridges, conveyors, paper machines etc
Resists +150°C dry heat and chemically active gases and dust
Withstands well immersion in water, oil and dilute solutions of non-oxidizing acids, alkalis and salts
Withstands immersion in mineral/vegetable/animal fats and oils
Available in a wide range of RAL & BS colours
Product customisation
Don't forget to save your customization to be able to add to cart
Temacoat GPL is a two-component, amine adduct cured mar and chemical resistant epoxy topcoat used especially as a finishing coat especially for objects exposed to heavy abrasion and chemical attack. Resists+150°C dry heat and chemically active gases and dust and, due to CE marking, it is also suitable for concrete surfaces in process industries.
Temacoat GPL withstands well immersion in water (+60ºC), oil and dilute solutions of non-oxidizing acids, alkalis and salts, with resistance to abrasion and chemicals making the surface retain its colour for a longer time
Recommended for bridges, tanks and different types of steelwork and equipment in the wood processing and chemical industries, such as tubular bridges, conveyors, paper machines etc
Used especially as a finishing coat especially for objects exposed to heavy abrasion and chemical attack.
Resists +150°C dry heat and chemically active gases and dust
Due to CE marking also suitable for concrete surfaces in process industries
Withstands well immersion in water, oil and dilute solutions of non-oxidizing acids, alkalis and salts
Wide colour range
Resistance to abrasion and chemicals makes the surface retain its colour for a longer time
Withstands +60ºC in immersion
Resists only temporary splashes of oxidizing acids and bleaching solutions
Withstands immersion in mineral/vegetable/animal fats and oils
Recommended for bridges, tanks and different types of steelwork and equipment in the wood processing and chemical industries, such as tubular bridges, conveyors, paper machines etc
Technical Data
Volume solids: 55±2% (ISO 3233)
Weight solids: 69±2%
Specific gravity: 1.3–1.4 kg / l (mixed) depending on colour
Pot life: 5 hours
VOC:
The Volatile Organic Compounds amount is 450 g/litre of paint mixture
VOC content of the paint mixture (thinned 10% by volume) is 490 g/l
Mixing ratio:
Base 3 parts by volume Temacoat GPL
Hardener 1 part by volume 008 7580
Recommended Film Thicknesses and Theoretical Coverage
Recommended film thicknesses
Theoretical coverage
Wet
Dry
90µm
50µm
11.0 m²/l
185µm
100µm
5.5 m²/l
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Drying Times
DFT 60µm
10°C
23°C
35°C
Dust dry, after
3h
2h
1h
Touch dry, after
10h
5h
2h
Recoatable, after
10h
4h
2h
Recoatable in immersion, after
32h
16h
8h
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Surface Preparation
Primed surfaces:
Oil, grease, salt and dirt are removed from the surface by appropriate means.
Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
Concrete surfaces:
The surface must be dry and at least 4 weeks old.
The relative humidity of the concrete should not exceed 97%.
Remove any splashes and unevennesses by grinding.
Remove laitance and form oil from concrete castings by sanding or blast cleaning.
Any cracks, crevices and voids must be repaired with a mixture of Temafloor 200 and fine dry quartz sand.
All surfaces must be clean, dry and free from contamination.
The temperature of the ambient air, surface and paint should not fall below +10ºC during application and drying.
Relative humidity of the air should not exceed 80% during application and drying.
The surface temperature of steel should remain at least 3°C above the dew point.
Good ventilation and sufficient air movement is required in confined areas during application and drying.
Note! There is a natural tendency of this coating to chalk, discolor or yellow unevenly. It is recommended to use polyurethane topcoat when there are high aesthetical requirements on colour appearance.
Mixing Components
First stir base and hardener separately.
The correct proportions of base and hardener must be mixed thoroughly before use. Use power mixer for mixing.
Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface and weaken the properties of the coating.
Application
For airless spraying, the product is thinned approximately 0–10%.
Recommended nozzle tip is 0.011"–0.017" and pressure 120–160 bar.
Spray angle shall be chosen according to the shape of the object.
For brush application product should be thinned according to the circumstances.
Thinners & Cleaners
Thinner 1031
Product Details
4685-766831
Data sheet
Manufacturer
Tikkurila
For Use By
Consumer Use
For Use On
Steel, Concrete
Application Method
Brush, Spray
Sheen
Gloss
Colour
Fully Tintable
Single, Two or Three Pack
Two-Pack
Pack Size
10L
Parts
2 component
Base Type
Epoxy
Minimum Applied Thickness
50µm (dry), 90µm (wet)
Maximum Applied Thickness
100µm (dry), 185µm (wet)
Solvent
Mixture - see safety sheet
Mixing Ratio
Base 3 parts by volume - Hardener 1 part by volume
Suitable Substrates
Steel, concrete
Key Features
Topcoat for objects exposed to heavy abrasion and chemical attack
Application
Brush, Spray
Touch Dry (at 20°C)
5 hours
Pot Life (at 20°C)
5 hours
Coverage
5.5 m²/l - 11.0 m²/l
Recommended Thinner/Cleaner
Thinner 1031
Unit Contents
Base, hardener
Compatible Primers
Temacoat GPL-S Primer, Temacoat GPL-S MIO, Temacoat SPA Primer, Temabond ST 200, Temabond ST 300, Temacoat Primer.
Compatible Topcoats
Temacoat GPL
Solids by Volume
55±2% (ISO 3233)
VOC
VOC content of the paint mixture (thinned 10% by volume) is 490 g/l
Customer agrees that before placing an Order, Customer has read and understood the most up to date Product Data Sheet for the Product. Where we have access to the Product Data Sheet from the manufacturer, we will either provide a copy on request, or include a link to the Product Data Sheet available on the manufacturer’s website. Customer further agrees that we have no liability for any errors or omissions contained within the Product Data Sheets. For more information, please see our Terms & Conditions of Sale.
Tikkurila Temacoat GPL is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
Tikkurila Temabond ST 200 is a two component high-solids, aluminium pigmented modified epoxy maintenance paint for demanding surfaces such as steel structures, railway vehicles, and infastructure in energy and telecommunications.Surface-tolerant high-solids epoxy paint. Very good adhesion even to hand-prepared steel. Lower VOC emissions...
Tikkurila Temabond ST 300 is a two-component high-solids, modified tintable epoxy maintenance paint for demanding surfaces, and is recommended for repairing of damages caused by transport or installation.Surface-tolerant with a wide colour range For steel and concrete surfaces Very good adhesion, even to hand-prepared steel Lower VOC...
Tikkurila Temacoat GPL-S MIO is a two-component, polyamide cured epoxy paint pigmented with micaceous iron oxide, with superior adhesion to steel surfaces forming a very strong and durable film that can be used as a primer or an intermediate coat in aggressive environmentsFast cure and low-temperature cure hardeners available - click to...
Tikkurila Temacoat GPL-S Primer is a two-component, polyamide-cured high build epoxy primer containing zinc phosphate.Excellent adhesion to steel, zinc and aluminium surfaces. Used as a primer or an intermediate coat in paint systems exposed to abrasion and chemical stress. Can be overcoated after a prolonged period of time. Faster...
A two-component resin modified epoxy paint containing anti-corrosive pigments that can be applied at sub-zero temperatures as a primer or an intermediate coat on surfaces exposed to climatic, mechanical and chemical stress.Recommended for building frameworks, tubular bridges, conveyors and other steelwork and equipment Adheres well to...
Tikkurila Temacoat SPA Primer, a two-component resin modified epoxy primer with anti-corrosive pigments with excellent adhesion to steel, zinc and aluminium surfaces, that can be applied in thick layers, thus enabling faster production.Has high solids content Used as a primer or an intermediate coat in paint systems exposed to abrasion...
These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3). Please click here for important information about these kits. Kit Contents: SET 1 (Hand Tools)1 x Rust-Oleum...