Temalac SC-F 40, a high-solids alkyd paint containing anti-corrosive pigments especially designed for use as a single-coat system on steel surfaces. The product protects the surface from corrosion and is recommended for steel framework, service platforms and different types of machinery and equipment.
Temalac SC-F 40 is a high-solids alkyd paint containing anti-corrosive pigments especially designed for use as a single-coat system on steel surfaces. The product protects the surface from corrosion and is recommended for steel framework, service platforms and different types of machinery and equipment.
For industrial and professional use only.
Volume solids
Weight solids
Specific gravity
VOC
| Recommended film thicknesses | Theoretical coverage | |
|---|---|---|
| Wet | Dry | |
| 160µm | 100µm | 6.1 m²/l |
| 200µm | 120µm | 5.1 m²/l |
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
| DFT 80µm | 10℃ | 23℃ | 35℃ |
|---|---|---|---|
| Dust dry, after | 30min | 20min | 10 min |
| Touch dry, after | 8h | 5h | 3h |
| Recoatable, after | 2 weeks | 1 week | 1 week |
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)
Steel surfaces:
Blast clean to grade Sa2½. (ISO 8501-1)
If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.
Primed surfaces:
Oil, grease, salt and dirt are removed from the surface by appropriate means.
Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
All surfaces must be clean and dry and free from contamination.
The temperature of the substrate should not fall below 5°C during application and drying.
Relative humidity of the air should not exceed 80% during application and drying.
The surface temperature of steel should remain at least 3°C above the dew point.
Good ventilation and sufficient air movement is required in confined areas during application and drying.
Stir the product carefully before use.
For airless spraying, the product is thinned approximately 0-5%.
Recommended nozzle tip is 0.011"–0.015" and pressure 160–200 bar.
Spray angle shall be chosen according to the shape of the object.
For conventional spraying, the product is thinned approximately 5–10%. Recommended nozzle tip is 1.6–1.8 mm and pressure 3–4 bar.
In order to reach thicker coats use "wet-on-wet" technique.
Customer agrees that before placing an Order, Customer has read and understood the most up to date Product Data Sheet for the Product. Where we have access to the Product Data Sheet from the manufacturer, we will either provide a copy on request, or include a link to the Product Data Sheet available on the manufacturer’s website. Customer further agrees that we have no liability for any errors or omissions contained within the Product Data Sheets. For more information, please see our Terms & Conditions of Sale.
Tikkurila Temalac SC-F 40 is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT
These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3). Please click here for important information about these kits. Kit Contents: SET 1 (Hand Tools)1 x Rust-Oleum...
£25.84 (incl. VAT)
£21.53 (ex. VAT)