Tikkurila Temasilox is a high performance, isocyanate free two-component, high-solids and high-gloss polysiloxane topcoat. Ideal for bridges, tanks, pipes, buildings, power plants, offshore structures and other structures that require long durability in severe corrosive atmospheric areas.
Huge colour range available.
Excellent anti-corrosive properties.
When applied in two-coat system on zinc rich primer, corrosivity class C5 can be achieved.
As a high-solids, VOC compliant product Temasilox meets even the most stringent environmental demands.
Higher UV-resistance than with conventional topcoats.
Can also be used as a single-coat finish on blast cleaned or phosphated steel. On blast cleaned steel even corrosivity category C4 is possible.
Product customisation
Don't forget to save your customization to be able to add to cart
Tikkurila Temasilox is a high performance, two-component, high-solids and high-gloss polysiloxane topcoat with excellent colour and gloss retention.
Recommended to be used as an isocyanate free finishing coating for steel structures for bridges, tanks, pipes, buildings, power plants, offshore structures and other structures that require long durability in severe corrosive atmospheric areas.
The anti-corrosive properties of Temasilox are outstanding. The product can be used as a single-coat paint or a topcoat. When applied in a two-coat system on zinc-rich primer, corrosivity class C5 can be achieved.
Temasilox is isocyanate free and does not, therefore, generate any di-isocyanates during cutting, welding or in a fire. The product promotes a healthier working environment and has less impact on the environment.
As a high-solids, VOC-compliant product, Temasilox meets even the most stringent environmental demands. Using Temasilox instead of conventional topcoats will result in a remarkable reduction in solvent emissions.
Excellent anticorrosive properties. When applied in two-coat system on zinc rich primer, corrosivity class C5 can be achieved.
Isocyanate free topcoat. Does not generate any di-isocyanates during cutting, welding or in a fire.
As a high-solids, VOC compliant product Temasilox meets even the most stringent environmental demands.
Higher UV-resistance than with conventional topcoats.
Offers significant savings with regard to maintenance costs.
Easy to apply on large surfaces due to long open time of the paint film.
No need for evaporation of solvents before ovening.
Rapidly ready for service.
The product is approved to be used as a topcoat in pre-qualified systems according to NORSOK M-501, system 1, rev.6.
Can also be used as a single-coat finish on blast cleaned or phosphated steel. On blast cleaned steel even corrosivity category C4 is possible.
Recommended to be used as an isocyanate free finishing coating for steel structures for bridges, tanks, pipes, buildings, power plants, offshore structures and other structures that require long durability in severe corrosive atmospheric areas.
Technical Data
Volume Solids: 87±2%.
Weight Solids:91±2%.
Specific Gravity: 1.5±0.1 kg / l (mixed).
Mixing Ratio:
Base - 2 parts by volume - Temasilox.
Hardener - 1 part by volume - 008 7601.
Pot Life (23°C): 2 hours.
Recommended Film Thicknesses and Theoretical Coverage:
Recommended film thicknesses
Theoretical coverage
Wet
Dry
90µm
80µm
10.9 m²/l
140µm
120µm
7.3 m²/l
170µm
150µm
5.8 m²/l
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Drying Time:
DFT 120 µm
5°C
10°C
23°C
50°C
70°C
Dust dry, after
1.5hrs
1hr
30min
-
-
Touch dry, after
2h
1hr 30min
1hr
-
-
Dry to handle, after
8hrs
5.5hrs
3hrs
1hr
25min
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation. When forced drying in temperatures 50–100ºC, use flash-off time between 0–15 minutes, depending on the wet film thickness and the actual temperature.
Gloss: High Gloss.
Colour Shades: RAL, NCS, BS, White.
Surface Preparation
Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4).
Steel Surfaces:
Blast clean to grade Sa2½–3. (ISO 8501-1)
If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.
Primed Surfaces:
Oil, grease, salt and dirt are removed from the surface by appropriate means.
Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4).
Customer agrees that before placing an Order, Customer has read and understood the most up to date Product Data Sheet for the Product. Where we have access to the Product Data Sheet from the manufacturer, we will either provide a copy on request, or include a link to the Product Data Sheet available on the manufacturer’s website. Customer further agrees that we have no liability for any errors or omissions contained within the Product Data Sheets. For more information, please see our Terms & Conditions of Sale.
Tikkurila Temasilox is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3). Please click here for important information about these kits. Kit Contents: SET 1 (Hand Tools)1 x Rust-Oleum...