Teamac 2 Pack Micaceous Iron Oxide is a High Build Epoxy based anti-corrosive protective paint for steel. Can be overcoated or left as a finish.
May be used as an intermediate coat or a finish coat onto a suitable primer. It can be used as a build coat in conjunction with Teamac 2 Pack Zinc Phosphate Primer to give much greater anti- corrosive protection to steel work. Ideal for use in marine and agricultural applications as well as harsh coastal environments.
Quick Links - Click To Jump To Section:
- Features & Benefits
- Product Data
- Drying Times
- Application Details
- Surface Preparation
- Mixing Instructions
- Application Conditions
- Preceding Coat
- Subsequent Coat
Features & Benefits
- High build
- Epoxy based
- Anti-corrosive
- Protective paint for steel
- Can be overcoated or left as a finish
- May be used as an intermediate coat or a finish coat onto a suitable primer
- Can be used as a build coat in conjunction with Teamac 2 Pack Zinc Phosphate Primer to give much greater anti-corrosive protection to steel work
- Ideal for use in marine and agricultural applications as well as harsh coastal environments
Product Data
Product Data | |
---|---|
Typical S.G. (Specific Gravity) | 1.65 @ 20 °C |
Volume Solids | 44% |
Wet Film Thickness W.F.T | 225 microns |
Dry Film Thickness D.F.T | 100 microns |
Expected Spreading Rate | 4.8 sq.m / litre @ 100 microns DFT |
The practical spreading rate may be lower as this depends on factors such as the porosity and roughness of the surface to be painted and material losses during application. | |
Typical Viscosity | N/A |
Flash Point | 25 °C (closed cup) |
Voc Content | 460g / litre |
Pot Life | 24 hours @ 20 °C |
Drying Times
Drying Time @ Recommended D.F.T | |
---|---|
Initial Cure | 30 mins @ 20 °C |
Hard Dry | 2 to 4 hours @ 20 °C |
Full Cure | 5 to 7 days @ 20 °C |
Low temperature and high humidity will adversely affect application, drying and performance of any coating. | |
Minimum Overcoating Time | 16 hours or overnight |
Application Details
Application Details | ||
---|---|---|
Application restrictions | Do not apply below 10 degree | |
Special conditions | Do not apply below 10°C or at humidity levels above 80 - to 90%. Mix Well and allow to stand for 20 minutes before use. | |
Method | Airless Spray | Brush (Small areas) |
Thinner (Max vol) | Do Not Thin | Do Not Thin |
Nozzle size | .021" - .027" | |
Nozzle pressure | 1800 to 2300 | |
Cleaning solvent | Thinners 39 | |
Recoat interval | Minimum 16 hours | Maximum 72 hours |
Surface Preparation
All surfaces should be clean, dry, sound and free from contaminants. Existing painted surfaces should be cleaned, degreased and sanded to ensure an adequate "key" is produced. Remove all loose, flaking material and treat bare areas as new substrate then prepare accordingly.
Mixing Instructions
By volume, mix 4 parts of the base with 1 part of the activator, as the ratio supplied. These should be thoroughly mixed together, preferably by slow speed electric mixer and allow to stand for 20 minutes before use. Ensuring the material is thoroughly mixed is very important - poorly mixed product can lead to soft spots and uncured coatings. Thinning is not normally required for airless spray systems. Use within 24 hours. Clean and flush equipment immediately after use to prevent the paint solidifying in guns, pots and lines.
Application Conditions
Should not be carried out when the ambient temperature is below 5 °C (Please note drying will be retarded below 10 °C but will stop below 5 °C) or the relative humidity is above 80 to 90%. As dictated by normal good painting practice. In confined spaces, provide adequate ventilation during application and drying.
Preceding Coat
Can be applied over Teamac 2 pack zinc phosphate primer which are free from contamination.
Subsequent Coat
Suitable Topcoat or leave as a finish.
Data sheet
- Manufacturer
- Teamac
- Water / Solvent Based
- Solvent
- For Use On
- Steel
- Application Method
- Spray, Brush
- Sheen
- Eggshell
- Colour
- Standard / Ready Mixed
- Single, Two or Three Pack
- Two-pack
- Pack Size
- 5KG
- Dry to Recoat (at 20°C)
- Minimum 16 hours
- Fully Cured (at 20°C)
- 5 to 7 days
- Pot Life (at 20°C)
- 24 hours
- Coverage
- 4.8 sq.m / litre @ 100 microns D.F.T
- Min. Application Temperature
- Do not apply below 10°C
- Solids by Volume
- 44
- VOC
- 460g / litre
- Recommended Dry Film Thickness
- 100 microns
- Recommended Wet Film Thickness
- 225 microns
- UN Number
- UN1263
- Specific Gravity
- 1.65 g / litre
- Hard Dry
- 2 to 4 hours @ 20 °C
- Brand
- Teamac
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
Teamac 2 Pack Micaceous Iron Oxide is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT