An engineered siloxane coating that embodies the properties of both a high performance epoxy and a polyurethane in one coat. General purpose high gloss coating offering good weathering and wear resistance. Provides a wipeable, durable surface that has good anti-graffiti properties for all mineral substrates.

Top Features & Benefits

• Very low odour.
• Gloss in appearance.
• Finish: Gloss.
• VOC: 8% by weight / 120g/l.
• Specific gravity: 1.36kg/l (mixed product).
• Pot life: 4 hours (200C).
• Drying times: at 125 µm dft and 200C in hours.
• 300C 200C 100C 50C.
• Dry to touch 1 2 4½ 7.
• Dry through 3 4½ 8½ 16.
• Mixing ratio (by volume): 4 parts resin: 1 part cure.

Product Use in the Workplace

Substrate Preparation
All loose, flaking and unstable material must be identified and then thoroughly removed, all surfaces must be thoroughly washed down with clean cold water to remove all surface dirt and dust. When all surfaces are clean, sound, wind dry, dust free and free from all surface contaminants, decoration using KEIM MX Glaze may proceed.

Application
KEIM MX Glaze is supplied in the proper mixing proportions of resin and cure. Add cure to resin and stir thoroughly with mechanical mixer for five minutes, avoid entrapment of air in the coating which will result in bubbles and blisters. Apply a thin and even coat by brush or short pile roller.

Application Conditions
Ambient and substrate temperature above 5°C and below 30°C. Do not apply in direct sunlight or onto sun-heated surfaces, nor if it is raining or if there is an immediate likelihood of rain.

Consumption
Approx. 0.1lt/m² per coat. Consumption rates are offered for guideline purposes only and are quoted for smooth surfaces. Actual rates are the responsibility of the applicator. Project specifications should be referred to for specific rates.

Cleaning of Tools
Clean tools with solvent immediately after use.