Rust-Oleum 9200 Rust-O-Thane Clear - CLEARANCE

Rust-Oleum 9200 Rust-O-Thane

Rust-Oleum 9200 Rust-O-Thane is a satin, water based polyurethane for a very durable and colourfast finish on metal. Rust-Oleum Rust-O-Thane 9200 is intended for application on substrates, which are coated with Rust-Oleum or Mathys epoxy or acrylic coatings (e.g. Rust-Oleum 9100 and Rust-Oleum 5401 Epoxy Impregnation Primer or Mathys Pegasol and Pegalink).

The application area consists of coated floors, coated walls and primed metal. Rust-Oleum 9200 Rust-O-Thane assures appropriate protection against solvents, moderate alkalines, weak acids and chemical cleaning.

Rust-Oleum 9200 Rust-O-Thane is especially recommended where general urethane performance like excellent weather resistance (UV), easy cleaning and abrasion resistance is required.

Rust-Oleum 9200 Rust-O-Thane is also suitable to be used on uPVC substrates.

Features & Benefits

• Available in 4,000+ RAL, NCS, and British Standard colours
• Very durable and UV-resistant, colour and gloss retention
• Very easy to clean (also with chemicals)
• Very low odour, can be used indoors
• High abrasion resistance, low wear
• Flexible and impact resistant
• Can also be used on floors and walls
• Suitable for use on uPVC

Technical Data 

• Density: 1,23
• Gloss Level: Satin
• Solids content in volume: 37 %
• Heat Resistance: 90°C (dry heat), above 65°C discoloration may occur
• Mixing Ratio: Base : Activator = 5.66 : 1 by volume

Drying Times At 20°C/RH 50%

• Touch dry: 2 hours
• Dry to handle: 4 hours
• Dry to recoat: 24 hours
• Fully cured: 2 days
• Pot Life: 2 hours for a 5 litre mix at 20°C
• Induction Time: 5 minutes

Theoretical Consumption

• 6,2 m²/l at 60 µm dry (depending on colour) for floors.
• 9,2 m²/l at 40 µm dry (depending on colour) for other applications.

Practical Consumption

Practical coverage depends on many factors such as porosity and roughness of the substrate and material losses during application.

Surface Preparation

Remove grease, oil and all other surface contamination using alkaline or high pressure (steam) cleaning in combination with appropriate detergents. Sand previous coatings that are in good condition to remove gloss and to roughen the surface slightly. Assure that the previous coating is compatible with the RUST-O-THANE 9200 by making a test application. Remove bad adhering coatings by scraping, wire brushing or sanding. (Spot)prime with commended Rust-Oleum or Mathys coatings. The surface must be clean and dry during application.

uPVC should be cleaned with a 5% solution of Rust-Oleum Mathys ND14 Cleaner Degreaser followed by a solvent wipe with Rust-Oleum Thinner 160. The surface should then be EITHER abraded, or primed with Rust-Oleum 3333 Super Adhesion Primer prior to application. 

Remarks

• Max dry film thickness for floors: 75 µm dry, equals 200 µm wet. For walls: 60 µm dry, equals 160 µm wet.
• For use on floors submitted to heavy abrasion, standard and medium colours are recommended. In case of deep and/or bright tones (red, yellow, orange, green, blue etc), it is advised to apply a clear topcoat.
• The product is not recommended in case of stagnating water and/or immersion

Now also available in convenient 1 litre packaging. Ideal for smaller projects the new convenient 2-component packaging provides the base and activator in one convenient kit and the activator is supplied with a user-friendly spout cap.

Please contact Rawlins Paints` Technical Support Team on 0113 2455450 for more information.