Tikkurila Temacoat GPL-S MIO is a two-component, polyamide cured epoxy paint pigmented with micaceous iron oxide, with superior adhesion to steel surfaces forming a very strong and durable film that can be used as a primer or an intermediate coat in aggressive environments
- Fast cure and low-temperature cure hardeners available - click to see more details
- Can be overcoated after a prolonged period of time
- Ideal for steel structures, bridges and equipment
- Robust and reliable
- Widely used in NORSOK and SSG approved systems
- Has an impressive track record in bridge construction and pulp, paper and power-industry projects
Tikkurila Temacoat GPL-S MIO is a two-component, polyamide cured epoxy paint pigmented with micaceous iron oxide.
Due to its micaceous iron-oxide pigmentation and superior adhesion to steel surfaces, Temacoat GPL-S MIO forms a very strong and durable film. It can be used as a primer or an intermediate coat in aggressive environments. With a special hardener, the paint cures even at sub-zero temperatures.
Temacoat GPL-S MIO can be overcoated after a prolonged period of time. Its property of not needing roughening saves time and reduces costs of the paint system application. The product is an ideal for steel structures, bridges and equipment.
Temacoat GPL-S MIO has an impressive track record in bridge construction and pulp, paper and power-industry projects. The paint is widely used in NORSOK and SSG approved systems.
Available with Hardener 008 5600; Faster Curing Hardener (008 5605) or Hardener for use in sub-zero temperatures (008 5610) available as POA subject to a 14-21 day lead time - call our sales team on 0113 2455450 or [email protected].
Quick Links - Click To Jump To Section:
- Features & Benefits
- Technical Data
- Surface Preparation
- Recommended Primers
- Recommended Topcoats
- Application Conditions
- Mixing Components
- Application
- Thinner/Cleaning
- VOC
- Health And Safety
Features & Benefits
- Forms a very strong and durable coat due to the micaceous iron oxide pigment.
- Excellent adhesion to steel surfaces.
- Used as a primer or intermediate coat in epoxy and polyurethane systems exposed to severe weathering and splashes.
- Rapidly recoatable.
- Can be overcoated after prolonged period.
- Hardener 008 5610 enables curing even at temperatures down to -10°C.
- Recommended for bridges, exteriors of tanks, steel frameworks, conveyors, tubular bridges and other steel structures and equipment.
Technical Data
Volume Solids: 60±2% (ISO 3233)
Weight Solids: 78±2%
Specific Gravity: 1.5 kg / l (mixed)
Pot Life:
- 4 hours (23 ºC) with Hardener 008 5600
- 2 hours (23 ºC) with Hardener 008 5605
- 4 hours (23ºC) with Hardener 008 5610
- 6 hours (0ºC) with Hardener 008 5610
Mixing Ratio
- Base - 4 parts by volume - Temacoat GPL-S MIO
- Hardener - 1 part by volume - 008 5600 or 008 5605 (fast)
- Base - 5 parts by volume - Temacoat GPL-S MIO
- Hardener - 1 part by volume - 008 5610 (for sub zero temperarures)
Recommended Film Thicknesses and Theoretical Coverage
Recommended film thicknesses | Theoretical coverage | |
---|---|---|
Wet | Dry | |
100µm | 60µm | 10.0 m²/l |
210µm | 125µm | 4.8 m²/l |
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Drying Times
Available with Hardener 008 5600; Faster Curing Hardener (008 5605) or Hardener for use in sub-zero temperatures (008 5610) available as POA subject to a 14-21 day lead time - call our sales team on 0113 2455450 or [email protected].
Hardener 008 5600 or 008 5605 | ||||||
---|---|---|---|---|---|---|
DFT 80 µm | 0°C | 5°C | 10°C | 23°C | 35°C | |
Dust dry, after | with Hardener 008 5600 | 4h | 2h | 1h | ½h | 15min |
with Hardener 008 5605 | 3h | 1½h | 45min | ½h | 12min | |
Touch dry, after | with Hardener 008 5600 | 18h | 10h | 6h | 2½h | 1½h |
with Hardener 008 5605 | 12h | 6h | 4h | 2h | 1h | |
Recoatable with epoxy paints, min. after | with Hardener 008 5600 | 24h | 12h | 6h | 2h | 1h |
with Hardener 008 5605 | 18h | 16h | 4h | 1½h | ¾h | |
Recoatable with polyurethane paints, min. after | with Hardener 008 5600 | 36h | 24h | 18h | 4h | 2h |
with Hardener 008 5605 | 24h | 12h | 8h | 3h | 1½h | |
Recoatable without roughening max. 6 months |
Hardener 008 5610 | |||||||
---|---|---|---|---|---|---|---|
-5°C | -10°C | 0°C | 5°C | 10°C | 23°C | 35°C | |
Dust dry, after | 16h | 10h | 4h | 2h | 1h | ½h | 15min |
Touch dry, after | 40h | 30h | 16h | 12h | 4h | 2h | 60min |
Recoatable, min. after | 74h | 62h | 40h | 28h | 14h | 8h | 5h |
Fully Cured | 28d | 21d | 18d | 6d | 4d | 4d | 3d |
Recoatable without roughening max. 2 months |
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Surface Preparation
Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)
Steel Surfaces:
- Blast clean to grade Sa2½. (ISO 8501-1) .
- If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.
Primed Surfaces:
- Oil, grease, salt and dirt are removed from the surface by appropriate means.
- Repair any damage to the primer coat.
- Note the overcoating time of primer.
Recommended Primers
- Temazinc 77
- Temazinc 99
- Temasil 90
- Temacoat GPL-S Primer
- Temabond ST 200
- Temabond ST 300
Recommended Topcoats
- Temacoat GPL
- Temacoat GS 50
- Temacoat RM 40
- Temadur 20
- Temadur 50
- Temadur 90
- Temathane 50
- Temathane 90
- Temathane PC 50
- Temathane PC 80
Application Conditions
With hardener 008 5600 or 008 5605 (fast):
- All surfaces must be clean, dry and free from contamination.
- During application and drying the temperature of the surface should not fall below 0°C.
- Relative humidity of the air should not exceed 80% during application and drying.
- The surface temperature of the steel should remain at least 3°C above the dew point.
- The product should not be applied at temperatures below 0°C where there is a possibility of ice formation on the substrate.
- For proper application the temperature of the paint itself should be above +15°C during mixing and application.
- Good ventilation and sufficient air movement is required in confined areas during application and drying.
With hardener 008 5610 (for sub zero temperartures):
- All surfaces must be clean and dry and free from contamination.
- During application and drying the temperature of the surface should not fall below -10°C.
- The surface temperature of steel should remain at least 3°C above the dew point.
- Care has to be taken that there is no ice on the substrate.
- For proper application the temperature of the paint itself should be above +15°C during mixing and application.
- Good ventilation and sufficient air movement is required in confined areas during application and drying.
Note! There is a natural tendency of this coating to chalk, discolor or yellow unevenly. It is recommended to use polyurethane topcoat when there are high aesthetical requirements on colour appearance.
Mixing Components
- First stir base and hardener separately.
- The correct proportions of base and hardener must be mixed thoroughly before use.
- Use power mixer for mixing.
- Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface and weaken the properties of the coating.
Application
- For airless spraying, the product is thinned approximately 0–10%.
- Recommended nozzle tip is 0.015"–0.021" and pressure 120–180 bar.
- Spray angle shall be chosen according to the shape of the object.
- For brush application product should be thinned according to the circumstances.
Thinner/Cleaning
VOC
The Volatile Organic Compounds amount is 340 g/litre of paint. VOC content of paint mixture (thinned 10% by volume) is 400 g/l.
Health And Safety
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets.
For industrial and professional use only.
Please contact Rawlins Paints' Technical Support Team on 0113 2455450 (option 2) or send a message to [email protected] for more information.
Data sheet
- Manufacturer
- Tikkurila
- Water / Solvent Based
- Solvent
- For Use On
- Steel
- Application Method
- Brush, spray
- Sheen
- Matt
- Colour
- Standard / Ready Mixed
- Single, Two or Three Pack
- Two-Pack
- Pack Size
- 20L
- Mixing Ratio
- 4:1 (5:1 with hardener 008 5610)
- Coverage
- 4.8 m²/l - 10.0 m²/l
- Recommended Thinner/Cleaner
- Thinner 1031
- Min. Application Temperature
- 0°C (-10°C with hardener 008 5610)
- Solids by Volume
- 60±2%
- VOC
- 400 g/l
- Recommended Dry Film Thickness
- 60µm - 125µm
- Recommended Wet Film Thickness
- 100µm - 210µm
- UN Number
- UN1263, UN3469
- Touch Dry (at 23°C)
- 2-2.5hrs (dependant on hardener used)
- Pot Life
- 4 hours (23 ºC) with Hardener 008 5600 and 008 5610 / 2 hours (23 ºC) with Hardener 008 5605
- Base Type
- Solvent-Based
- Suitable For Use On
- Steel
- Finish
- Matt
- Application Method
- Brush
- Application Method
- Spray
- Usages
- MIO
- Product Usage Type
- Primer
- Product Range
- Temacoat
- Colour Family
- Red
- Colour Family
- Grey
- Dry to Recoat (@ 20-25°C)
- 8 hours
Questions
Question about the product
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
Tikkurila Temacoat GPL-S MIO is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT
Tikkurila Temabond ST 200
2 component high-solids, aluminium pigmented modified epoxy maintenance paint for demanding surfaces such as steel structures, railway vehicles, and infastructure in energy and telecommunications. Surface-tolerant high-solids epoxy paint. Very good adhesion even to hand-prepared steel. Lower VOC emissions than conventional epoxy paints....
Tikkurila Temabond ST 300
Tikkurila Temabond ST 300 is a two-component high-solids, modified tintable epoxy maintenance paint for demanding surfaces, and is recommended for repairing of damages caused by transport or installation. Surface-tolerant with a wide colour range For steel and concrete surfaces Very good adhesion, even to hand-prepared steel Lower VOC...
Tikkurila Temacoat GPL
Temacoat GPL, a two-component, amine adduct cured mar and chemical resistant epoxy topcoat used especially as a finishing coat especially for objects exposed to heavy abrasion and chemical attack. Due to CE marking it is also suitable for concrete surfaces in process industries. Recommended for bridges, tanks and different types of...
Tikkurila Temacoat GS 50
Tikkurila Temacoat GS 50, a two-component, polyamide-cured high build epoxy finishing and intermediate coat for protection of steel framework, conveyors, tubular bridges and other steel structures from abrasion and mechanical and/or chemical stress. Fast cure hardener available on request Can also be used as a sealer or a single-coat paint...
Tikkurila Temacoat RM 40
2-component, resin modified epoxy primer/topcoat with 4,000+ colours that can be used as a single-coat system. Good adhesion to steel, zinc and aluminium surfaces exposed to severe abrasion or chemical stress. Suitable for concrete surfaces and has a CE marking. Can be used on steel structures in wet environments, e.g. inside pontoons,...
Tikkurila Temadur 20
2-pack semi-matt polyurethane paint with 3,800+ colours that can be used as a single-coat paint for steel, zinc and aluminium surfaces with its anti-corrosion pigmentation, and also used as a primer or as a semi-matt topcoat in epoxy-polyurethane systems. It is also suitable for use on uPVC. Resistance to weathering and abrasion MED...
Tikkurila Temadur 50
Time-proven, easy-to-use general purpose topcoat in 4,000+ colours for constructional steelwork and machinery, with a wide range of colours to choose from. Two-component, durable and non-chalking semi-gloss polyurethane paint, hardener aliphatic isocyanate. Forms a durable, easy-to-clean and non-chalking topcoat with good gloss and colour...
Tikkurila Temadur 90
Tikkurila Temadur 90, 2-pack, high gloss polyurethane paint recommended to be used as a glossy decorative finishing coat for epoxy systems on a variety of substrates such as steel, aluminium, concrete etc. exposed to severe weathering and/or chemical stress. Forms a durable, easy-to-clean and non-chalking topcoat with outstanding gloss and...
Tikkurila Temazinc 99
Tikkurila Temazinc 99, a 2-component, polyamide cured zinc-rich epoxy paint providing superior cathodic protection for steel, used as a primer in epoxy, polyurethane, acrylic and chlorinated rubber systems for steel surfaces exposed to severe climatic conditions. Prequalified in the NORSOK system 1; an excellent choice for the most...
Tikkurila Temasil 90
Tikkurila Temasil 90 is a two-component ethyl silicate zinc rich paint. Protective coating with an effect similar to that achieved with galvanizing. Can be used as a single coat or as a primer in protective coating systems. Excellent resistance to abrasion and weathering. Offers cathodic protection of steel. Can be used on steel...
Tikkurila Thinner 1031
Tikkurila Thinner 1031 is a thinner for epoxy paints, silicone paints, polyvinylbutyral paints, 2-component zinc rich paints and epoxy shop primers.
Tikkurila Temazinc 77
Tikkurila Temazinc 77, a primer with good cathodic protection for steel containing over 80% zinc, fully meeting requirements of the standard ISO 1294-5 for zinc-rich primers. Used in coating systems where extended durability is required Used as a primer in epoxy, polyurethane, acrylic and chlorinated rubber systems for steel surfaces...
Tikkurila Temathane PC 50
Tikkurila Temathane PC 50, a high-solids two-component, semi-gloss polyurethane paint, hardener aliphatic isocyanate recommended for painting of storage tank exteriors, steel buildings and other steelwork. Huge colour range available, with RAL, BS & NCS shades Prequalified in the NORSOK system 1 and therefore an excellent choice for...
Tikkurila Temathane PC 80
Tikkurila Temathane PC 80, a high-solids two-component, glossy polyurethane paint (with hardener aliphatic isocyanate) that is particularly suitable for harsh environments, helping extend the service life of the paint system. Huge colour range with RAL, BS & NCS shades Excellent choice when a high-solids topcoat with extremely good...
Tikkurila Temathane 50
Tikkurila Temathane 50 is a two-component, semi-gloss polyurethane paint, hardener aliphatic isocyanate. Dries rapidly and is easy to apply. Recommended to be used as a semi-gloss topcoat for epoxy and polyurethane systems exposed to weathering. A durable, easy to clean and non-chalking topcoat. Excellent weathering and abrasion...
Tikkurila Temathane 90
Tikkurila Temathane 90 is a two-component, glossy polyurethane paint, hardener aliphatic isocyanate. The paint is used as a glossy topcoat for epoxy and polyurethane systems exposed to weathering. Forms a durable, easy-to-clean and non-chalking finish. Suitable for painting the outside of storage tanks, steel building and other steelwork....
Surface Preparation Kits for Steel
These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3). Please click here for important information about these kits. Kit Contents: SET 1 (Hand Tools) 1 x Rust-Oleum...