Tikkurila Temacoat GPL-S Primer is a two-component, polyamide-cured high build epoxy primer containing zinc phosphate.
- Excellent adhesion to steel, zinc and aluminium surfaces.
- Used as a primer or an intermediate coat in paint systems exposed to abrasion and chemical stress.
- Can be overcoated after a prolonged period of time.
- Faster Curing Hardener (008 5605) or Hardener for use in sub-zero temperatures (008 5610) available as POA subject to a 14-21 day lead time - call our sales team on 0113 2455450 or [email protected]
- Recommended usage areas are bridges, haulage equipment, cranes, steel masts, conveyors and other steelwork, machinery and equipment.
Product customisation
Don't forget to save your customization to be able to add to cartTikkurila Temacoat GPL-S Primer is a two-component, polyamide-cured high build epoxy primer containing zinc phosphate.
Rapidly recoatable Temacoat GPL-S Primer is used as a primer or an intermediate coat in paint systems exposed to abrasion and chemical stress. The paint adheres extremely well to steel, zinc and aluminium surfaces making it a universal, all-round primer for various applications.
With a special hardener, Temacoat GPL-S Primer cures even at sub-zero temperatures and it can be overcoated after a prolonged period of time. The recommended usage areas are bridges, haulage equipment, cranes, steel masts, conveyors and other steelwork, machinery and equipment.
Temacoat GPL-S Primer has a MED certificate and is thus accepted for painting interior ship surfaces. The primer can be tinted to various of colors, which helps achieve the best possible hiding power for the topcoat.
With hardener 008 5610 Temacoat GPL-S Primer enables curing even at temperatures down to -10°C.
Also available in 200L in TVT 4002. Please contact us for more information. Available with Hardener 008 5600; Faster Curing Hardener (008 5605) or Hardener for use in sub-zero temperatures (008 5610) available as POA subject to a 14-21 day lead time - call our sales team on 0113 2455450 or [email protected]
Quick Links - Click To Jump To Section:
- Features & Benefits
- Technical Data
- Surface Preparation
- Recommended Primers
- Recommended Topcoats
- Application Conditions
- Mixing Components
- Application
- Thinner/Cleaning
- VOC
- Health And Safety
Features & Benefits
- Rapidly recoatable Temacoat GPL-S Primer is used as a primer or an intermediate coat in paint systems exposed to abrasion and chemical stress.
- The paint adheres extremely well to steel, zinc and aluminium surfaces making it a universal, all-round primer for various applications.
- With a special hardener, Temacoat GPL-S Primer cures even at sub-zero temperatures and it can be overcoated after a prolonged period of time.
- The product has MED (Marine Equipment Directive) certificate no EUFI29-19002494- MED and is thus accepted for painting surfaces inside the ships.
- The primer can be tinted to various of colors, which helps achieve the best possible hiding power for the topcoat.
- Can be used as an intermediate coat on zinc-rich epoxy and zinc silicate paints.
- Rapidly recoatable.
- Recommended for bridges, haulage equipment, cranes, steel masts, conveyors and other steelwork, machinery and equipment.
Technical Data
Volume Solids: 55±2% (ISO 3233)
Weight Solids: 68±2%
Specific Gravity: 1.3–1.4 kg / l (mixed)
Mixing Ratio
- Base - 4 parts by volume - Temacoat GPL-S Primer
- Hardener - 1 part by volume - 008 5600 or 008 5605 (fast)
- Base - 5 parts by volume - Temacoat GPL-S Primer
- Hardener - 1 part by volume - 008 5610 (for sub zero temperarures)
Recommended Film Thicknesses and Theoretical Coverage:
Recommended film thicknesses | Theoretical coverage | |
---|---|---|
Wet | Dry | |
110µm | 60µm | 9.0 m²/l. |
185µm | 100µm | 5.5 m²/l. |
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Drying Time:
Available with Hardener 008 5600; Faster Curing Hardener (008 5605) or Hardener for use in sub-zero temperatures (008 5610) available as POA subject to a 14-21 day lead time - call our sales team on 0113 2455450 or [email protected].
Hardener 008 5600 or 008 5605 | ||||||
---|---|---|---|---|---|---|
DFT 60 µm | 0°C | 5°C | 10°C | 23°C | 35°C | |
Dust dry, after | Hardener 008 5600 | 4h | 2h | 1h | ½h | 15min |
Hardener 008 5605 | 3h | 1½h | 45min | ½h | 12min | |
Touch dry, after | Hardener 008 5600 | 16h | 8h | 4h | 2½h | 1h |
Hardener 008 5605 | 12h | 6h | 3h | 1½h | ½h | |
Recoatable with epoxy paints, min. after | Hardener 008 5600 | 16h | 6h | 4h | 2h | 45min |
Hardener 008 5605 | 12h | 5h | 3h | 1½h | ½h | |
Recoatable with polyurethane paints, min. after | Hardener 008 5600 | 24h | 8h | 5h | 2h | 1h |
Hardener 008 5605 | 16h | 6h | 4h | 1½h | 45min | |
Recoatable without roughening max. 6 months |
Hardener 008 5610 | |||||||
---|---|---|---|---|---|---|---|
DFT 60 µm | -10°C | -5°C | 0°C | 5°C | 10°C | 23°C | 35°C |
Dust dry, after | 16h | 10h | 4h | 2h | 1h | ½h | 15min |
Touch dry, after | 40h | 30h | 12h | 8h | 3h | 1½h | 30min |
Recoatable, min after | 48h | 36h | 14h | 10h | 4h | 2h | 1h |
Full cure | 28d | 21d | 18d | 6d | 4d | 4d | 3d |
Recoatable without roughening max. 2 months |
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Surface Preparation
Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)
Steel Surfaces:
- Blast clean to grade Sa2½. (ISO 8501-1) .
- If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.
Zinc Surfaces:
- Sweep blast clean with mineral abrasives, e.g. quartz sand, to an even roughness.
- If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with Panssaripesu detergent.
Aluminium Surfaces:
- Sweep blast clean with non-metallic abrasives to an even roughness.
- If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with MAALIPESU detergent
Stainless Steel:
- Roughen the surface by grinding or sweep blasting using non-metallic abrasives.
Primed Surfaces:
- Oil, grease, salt and dirt are removed from the surface by appropriate means.
- Repair any damage to the primer coat.
- Note the overcoating time of primer.
Note! Hardener 008 5610 is to be used only in steel or primed surfaces.
Recommended Primers
- Temabond ST 200
- Temacoat GPL-S Primer
- Temazinc 77
- Temasil 90
- Temabond ST 300
Recommended Topcoats
- Fontecoat EP 50
- Fontecoat EP 80
- Temacoat GPL
- Temacoat GS 50
- Temacoat RM 40
- Temacoat SPA 50
- Temadur 10
- Temadur 20
- Temadur 50
- Temadur 90
- Temadur HS 90
- Temadur SC-F 20
- Temadur SC-F 50
- Temadur SC-F 80
- Temathane 50
- Temathane 90
- Temathane PC 50
- Temathane PC 80
Application Conditions
With hardener 008 5600 or 008 5605 (fast):
- All surfaces must be clean, dry and free from contamination.
- During application and drying the temperature of the substrate should be minimum 0°C and relative humidity of the air should not exceed 80%..
- The surface temperature of the steel should be at least 3°C above the dew point.
- The product should not be applied at temperatures below 0°C where there is a possibility of ice formation on the substrate.
- The temperature of paint itself should be above +15°C for proper application.
- Good ventilation is required in confined areas during application and drying.
With hardener 008 5610 (for sub zero temperatures):
- All surfaces must be clean and dry and free from contamination.
- During application and drying the temperature of the surface should not fall below -10°C.
- The surface temperature of steel should remain at least 3°C above the dew point.
- Care has to be taken that there is no ice on the substrate.
- For proper application the temperature of the paint itself should be above +15°C during mixing and application.
- Good ventilation and sufficient air movement is required in confined areas during application and drying.
Note! There is a natural tendency of this coating to chalk, discolor or yellow unevenly. It is recommended to use polyurethane topcoat when there are high aesthetical requirements on colour appearance.
Mixing Components
- First stir base and hardener separately.
- The correct proportions of base and hardener must be mixed thoroughly before use.
- Use power mixer for mixing.
- Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface and weaken the properties of the coating.
Application
- For airless spraying, the product is thinned approximately 0–15%.
- Recommended nozzle tip is 0.011"–0.017" and pressure 120–160 bar.
- Spray angle shall be chosen according to the shape of the object.
- Use brush application only for stripe coating. For brush application the product should be thinned according to the circumstances.
Thinner/Cleaning
VOC
The Volatile Organic Compounds amount is 425 g/litre of paint mixture. VOC content of the paint mixture (thinned 15% by volume) is 485 g/l.
Health And Safety
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets.
For industrial and professional use only.
Please contact Rawlins Paints' Technical Support Team on 0113 2455450 (option 2) or send a message to [email protected] for more information.
Data sheet
- Manufacturer
- Tikkurila
- Interior / Exterior Use
- Interior & Exterior
- Water / Solvent Based
- Solvent
- For Use On
- steel, zinc, aluminium
- Application Method
- Spray, brush
- Sheen
- Matt
- Colour
- Fully Tintable
- Single, Two or Three Pack
- Two-Pack
- Pack Size
- 3L, 20L
- Base Type
- Epoxy
- Interior/Exterior Use
- Both
- Solvent
- Mixture (see Safety Data Sheet)
- Mixing Ratio
- 4:1 (5:1 with hardener 008 5610)
- Coverage
- 5.5 m²/l - 9.0 m²/l
- Recommended Thinner/Cleaner
- Thinner 1031
- Min. Application Temperature
- 0°C
- Solids by Volume
- 55±2%
- VOC
- 485 g/l
- Recommended Dry Film Thickness
- 60µm - 100µm
- Recommended Wet Film Thickness
- 110µm - 185µm
- UN Number
- UN1263, UN3469
- Dry to Recoat (at 23°C)
- 1.5-2hrs
- Touch Dry (at 23°C)
- 1.5-2.5hrs (dependant on hardener used)
- Pot Life
- 4hrs with hardeners 008 5600 and 008 5610. 2hrs with hardener 008 5605 (+23ºC)
- Base Type
- Epoxy
- Base Type
- Solvent-Based
- Suitable For Use On
- Zinc
- Suitable For Use On
- Aluminium
- Suitable For Use On
- Stainless Steel
- Suitable For Use On
- Steel
- Suitable For Use On
- Galvanised Steel
- Suitable For Use On
- Zinc Silicate
- Suitable For Use On
- Primed Surfaces
- Suitable For Use On
- Zinc Rich Epoxy
- Finish
- Matt
- Application Method
- Brush
- Application Method
- Spray
- Usages
- Intermediate
- Usages
- High Build
- Usages
- Low Temperature
- Usages
- Atmospheric
- Usages
- Zinc Phosphate
- Product Usage Type
- Primer
- Product Range
- Temacoat
- Colour Family
- Anthracite Grey
- Colour Family
- Beige
- Colour Family
- Grey
- Colour Family
- Green
- Colour Family
- Blue
- Colour Family
- Red
- Colour Family
- Brown
- Colour Family
- Pink
- Colour Family
- Orange
- Colour Family
- Purple
- Colour Family
- Yellow
- Colour Family
- Black
- Colour Family
- White
- Dry to Recoat (@ 20-25°C)
- 2 hours
- Categorised As
- Metal Paints > Low Temperature Primers
- Seasonal
- Cold Weather
- Industry Approved System
- MED
Questions
Question about the product
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
Tikkurila Temacoat GPL-S Primer is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT
Tikkurila Fontecoat EP 50
Tikkurila Fontecoat EP 50, a two-component water-borne epoxy topcoat and a single-coat paint recommended for framework, service platforms, conveyors and other steelwork, machinery and equipment. The product has MED (Marine Equipment Directive) certificate no VTT-C-12360-15-18 and is thus accepted for painting surfaces inside ships. Huge...
Tikkurila Fontecoat EP 80
Tikkurila Fontecoat EP 80, a two-component water-borne epoxy topcoat for low VOC demands that can be used as a glossy topcoat in epoxy paint systems for steel surfaces. Huge colour range from RAL, BS & NCS Forms a tough and glossy surface with high resistance to abrasion and chemical stress Low VOC emissions Can be used with...
Tikkurila Temabond ST 200
2 component high-solids, aluminium pigmented modified epoxy maintenance paint for demanding surfaces such as steel structures, railway vehicles, and infastructure in energy and telecommunications. Surface-tolerant high-solids epoxy paint. Very good adhesion even to hand-prepared steel. Lower VOC emissions than conventional epoxy paints....
Tikkurila Temabond ST 300
Tikkurila Temabond ST 300 is a two-component high-solids, modified tintable epoxy maintenance paint for demanding surfaces, and is recommended for repairing of damages caused by transport or installation. Surface-tolerant with a wide colour range For steel and concrete surfaces Very good adhesion, even to hand-prepared steel Lower VOC...
Tikkurila Temacoat GPL
Temacoat GPL, a two-component, amine adduct cured mar and chemical resistant epoxy topcoat used especially as a finishing coat especially for objects exposed to heavy abrasion and chemical attack. Due to CE marking it is also suitable for concrete surfaces in process industries. Recommended for bridges, tanks and different types of...
Tikkurila Temacoat GS 50
Tikkurila Temacoat GS 50, a two-component, polyamide-cured high build epoxy finishing and intermediate coat for protection of steel framework, conveyors, tubular bridges and other steel structures from abrasion and mechanical and/or chemical stress. Fast cure hardener available on request Can also be used as a sealer or a single-coat paint...
Tikkurila Temacoat RM 40
2-component, resin modified epoxy primer/topcoat with 4,000+ colours that can be used as a single-coat system. Good adhesion to steel, zinc and aluminium surfaces exposed to severe abrasion or chemical stress. Suitable for concrete surfaces and has a CE marking. Can be used on steel structures in wet environments, e.g. inside pontoons,...
Tikkurila Temacoat SPA 50
Tikkurila Temacoat SPA 50 is a two-component resin modified epoxy paint that can be applied to steel, zinc and aluminium as an excellent primer, intermediate or finish coat on surfaces exposed to stress and is also suitable as a single-coat system. Rapidly recoatable and ready to handle paint Forms durable film with good mechanical,...
Tikkurila Temadur 10
Tikkurila Temadur 10, a two-component matt polyurethane paint containing anti-corrosive pigments used as a single-coat paint for steel, zinc and aluminium surfaces. Huge colour range available with RAL, BS & NCS shades Can also used as a primer or a matt topcoat in epoxy systems exposed to weathering and/or chemical stress...