A two-component resin modified epoxy paint containing anti-corrosive pigments that can be applied at sub-zero temperatures as a primer or an intermediate coat on surfaces exposed to climatic, mechanical and chemical stress.
- Recommended for building frameworks, tubular bridges, conveyors and other steelwork and equipment
- Adheres well to steel, zinc and aluminium surfaces
- It is possible to achieve high film thickness with one application
- The product is used as an intermediate coat in the NORSOK approved systems on surfaces exposed to marine conditions
- Fast & low-temperature curing hardener (008 5613) available on request (extra charges may apply)
- Pigmented with zinc phosphate
Product customisation
Don't forget to save your customization to be able to add to cartTikkurila Temacoat Primer is a two-component resin modified epoxy paint containing anti-corrosive pigments that adheres well to steel, zinc and aluminium surfaces, ensuring a long service life for paint systems in severe environments.
The high-build primer can be applied at sub-zero temperatures and is used as a primer or an intermediate coat on surfaces exposed to climatic, mechanical and chemical stress.
The product is used as an intermediate coat in the NORSOK approved systems on surfaces exposed to marine conditions, and is recommended for building frameworks, tubular bridges, conveyors and other steelwork and equipment.
Fast & low-temperature curing hardener (008 5613) available on request; contact our sales team on 0113 2455450 or [email protected] to discuss your project requirements.
For industrial and professional use only.
Quick Links - Click To Jump To Section:
- Features & Benefits
- Case Studies
- Technical Data
- Surface Preparation
- Recommended Primers
- Recommended Topcoats
- Application Conditions
- Mixing Components
- Application
- Thinners & Cleaners
Features & Benefits
- Adheres well to steel, zinc and aluminium surfaces
- It is possible to achieve high film thickness with one application
- The high-solids product ensures a long service life for the paint system
- A high-build primer for paint systems used in severe environments
- The product is used as an intermediate coat in the NORSOK approved systems on surfaces exposed to marine conditions
- The speed of the painting process can be adjusted by choice of hardener
- Can be applied at sub-zero temperatures
- Used as a primer or an intermediate coat on surfaces exposed to climatic, mechanical and chemical stress
- Pigmented with zinc phosphate
- Recommended for building frameworks, tubular bridges, conveyors and other steelwork and equipment
Case Studies
The steel structures of the world’s largest indoor ski centre in Norway are manufactured by Ruukki and protected with Tikkurila's polyurethane system TP131, which consists of anti-corrosive Temacoat Primer and high-solids polyurethane topcoat Temathane PC 50. The combination provides excellent weather and abrasion resistance for steel, stainless steel, aluminum and zinc surfaces.
Under construction at Lørenskog, Norway (approx. 20km east of Oslo), six-story skiing complex is the world's largest indoor ski center with a snow-covered area of around 40,000 square meters (the equivalent of five football pitches) comprising of a 500m long downhill ski slope, equipped with three ski lifts, and a cross-country ski track suspended from the ceiling with 150 components and weighs about 500 tonnes.
The steel structures are coated with Tikkurila's polyurethane system TP131. Quality standards for the ski center's steel structures and protective coatings are very high; the minimum structural steel grade was S355, but certain structures of longer span distances required S550 high-strength steels. Protective coatings had to meet corrosion class C3 H according to EN-12944.
Technical Data
- Volume Solids: 72±2% (ISO 3233)
- Weight Solids: 83±2%
- Specific Gravity: 1.3 - 1.4 kg / l (mixed)
- VOC:
- The Volatile Organic Compounds amount is 280 g/litre of paint mixture.
- VOC content of the paint mixture (thinned 10% by volume) is 325 g/l.
- Mixing Ratio:
- Base 4 parts by volume Temacoat Primer
- Hardener 1 part by volume 008 5611
- Base 5 parts by volume Temacoat Primer
- Hardener 1 part by volume 008 5613
- Pot Life (at 23℃)
- 6 hours with Hardener 008 5611
- 4 hours with Hardener 008 5613
Recommended Film Thicknesses and Theoretical Coverage
Recommended film thicknesses | Theoretical coverage | |
---|---|---|
Wet | Dry | |
110µm | 225µm | 9.0 m²/l |
80µm | 160µm | 4.5 m²/l |
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Drying Times
Fast & low-temperature curing hardener (008 5613) available on request; contact our sales team on 0113 2455450 or [email protected] to discuss your project requirements.
DFT 100 µm | -10°C | -5°C | 0°C | 10°C | 23°C | 35°C | |
---|---|---|---|---|---|---|---|
Dust dry, after | with Hardener 008 5611 | - | - | 20h | 5h | 3h | 1½h |
with Hardener 008 5613 | 16h | 10h | 6h | 4½h | 1h | ½h | |
Touch dry, after | with Hardener 008 5611 | - | - | 30h | 12h | 5h | 3h |
with Hardener 008 5613 | 30h | 16h | 11h | 7h | 3h | 1½h | |
Recoatable, min. after | with Hardener 008 5611 | - | - | 32h | 12h | 4h | 2h |
with Hardener 008 5613 | 24h | 12h | 8h | 5h | 3h | 1h | |
Recoatable with polyurethane paints, min. after | with Hardener 008 5611 | - | - | 2½d | 18h | 6h | 3h |
with Hardener 008 5613 | 30h | 16h | 10h | 6h | 4h | 2h | |
Recoatable without roughening max. 3 months |
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Surface Preparation
Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)
Steel surfaces:
- Blast clean to grade Sa2½. (ISO 8501-1)
- If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.
Zinc surfaces:
- Sweep blast clean with mineral abrasives, e.g. quartz sand, to an even roughness. (SaS, SFS 5873)
- If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with Panssaripesu detergent.
- For hot dip galvanized surfaces see separate application instructions or contact Tikkurila Technical Service/Rawlins Technical on 0113 2455450 (option 2) or send a message to [email protected]
Aluminium surfaces:
- Sweep blast clean with non-metallic abrasives to an even roughness. (SaS, SFS 5873)
- If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with Maalipesu detergent.
Primed surfaces:
- Oil, grease, salt and dirt are removed from the surface by appropriate means.
- Repair any damage to the primer coat.
- Note the overcoating time of primer. (ISO 12944-4)
Recommended Primers
- Temazinc 99
- Temacoat Primer
- Temazinc 77
Recommended Topcoats
- Temacoat GPL
- Temadur 10
- Temacoat GS 50
- Temacoat GPL-S MIO
- Temadur HS 90
- Temadur SC-F 20
- Temadur SC-F 50
- Temadur SC-F 80
- Temathane 50
- Temathane 90
- Temathane PC 50
- Temathane PC 80
- Temasilox
- Temacryl EA 50
Application Conditions
With hardener 008 5611:
- All surfaces must be clean, dry and free from contamination.
- During application and drying the temperature of the surface should not fall below 0°C.
- The surface temperature of steel should remain at least 3°C above the dew point.
- Relative humidity of the air should not exceed 80% during application and drying.
- The product should not be applied at temperatures below 0°C when there is a possibility of ice formation on the substrate.
- For proper application the temperature of the product itself should be above +15°C during mixing and application.
- Good ventilation and sufficient air movement is required in confined areas during application and drying.
With hardener 008 5613:
Hardener (008 5613) available on request; contact our sales team on 0113 2455450 or [email protected] to discuss your project requirements.
- All surfaces must be clean, dry and free from contamination.
- During application and drying the temperature of the surface should not fall below -10°C.
- The surface temperature of steel should remain at least 3°C above the dew point.
- Care has to be taken that there is no ice on the substrate.
- For proper application the temperature of the product itself should be above +15°C during mixing and application.
- Good ventilation and sufficient air movement is required in confined areas during application and drying.
Note! There is a natural tendency of this coating to chalk, discolor or yellow unevenly. It is recommended to use polyurethane topcoat when there are high aesthetical requirements on colour appearance.
Mixing Components
- First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use.
- Use power mixer for mixing.
- Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface and weaken the properties of the coating.
Application
- For airless spraying, the product is thinned approximately 0–10%.
- Recommended nozzle tip is 0.015"–0.021" and pressure 120–180 bar.
- Spray angle shall be chosen according to the shape of the object.
- For brush application product should be thinned according to the circumstances.
Thinners & Cleaners
For cleaning, use Thinner 006 1031.
Data sheet
- Manufacturer
- Tikkurila
- For Use On
- Steel, Zinc, Aluminium
- Application Method
- Brush, Spray
- Sheen
- Semi Matt
- Colour
- Standard / Ready Mixed
- Single, Two or Three Pack
- Two-Pack
- Pack Size
- 20L
- Min. Application Temperature
- (-10°C)
- UN Number
- UN1263
- Base Type
- Solvent-Based
- Base Type
- Epoxy
- Suitable For Use On
- Zinc
- Suitable For Use On
- Aluminium
- Suitable For Use On
- Steel
- Finish
- Semi-Matt
- Application Method
- Brush
- Application Method
- Spray
- Usages
- High Solids
- Usages
- High Build
- Usages
- Low Temperature
- Usages
- Atmospheric
- Usages
- Anti-Corrosive
- Usages
- Zinc Phosphate
- Usages
- Intermediate
- Product Usage Type
- Primer
- Product Range
- Temacoat
- Colour Family
- Grey
- Dry to Recoat (@ 20-25°C)
- 6 hours
- Product Focus
- Mould & Damp Proof Paints
- Seasonal
- Cold Weather
- Industry Approved System
- Norsok
Questions
Question about the product
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
Tikkurila Temacoat Primer is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT

Tikkurila Temacoat GPL-S MIO
Tikkurila Temacoat GPL-S MIO is a two-component, polyamide cured epoxy paint pigmented with micaceous iron oxide, with superior adhesion to steel surfaces forming a very strong and durable film that can be used as a primer or an intermediate coat in aggressive environments Fast cure and low-temperature cure hardeners available - click to...

Tikkurila Temacoat GPL
Temacoat GPL, a two-component, amine adduct cured mar and chemical resistant epoxy topcoat used especially as a finishing coat especially for objects exposed to heavy abrasion and chemical attack. Due to CE marking it is also suitable for concrete surfaces in process industries. Recommended for bridges, tanks and different types of...

Tikkurila Temacoat GS 50
Tikkurila Temacoat GS 50, a two-component, polyamide-cured high build epoxy finishing and intermediate coat for protection of steel framework, conveyors, tubular bridges and other steel structures from abrasion and mechanical and/or chemical stress. Fast cure hardener available on request Can also be used as a sealer or a single-coat paint...

Tikkurila Temacoat Primer
A two-component resin modified epoxy paint containing anti-corrosive pigments that can be applied at sub-zero temperatures as a primer or an intermediate coat on surfaces exposed to climatic, mechanical and chemical stress. Recommended for building frameworks, tubular bridges, conveyors and other steelwork and equipment Adheres well to...