Tikkurila Temathane PC 50, a high-solids two-component, semi-gloss polyurethane paint, hardener aliphatic isocyanate recommended for painting of storage tank exteriors, steel buildings and other steelwork.
- Huge colour range available, with RAL, BS & NCS shades
- Prequalified in the NORSOK system 1 and therefore an excellent choice for the most demanding application areas such as offshore environments, refineries, power plants and bridges
- Forms easy-to-clean and non-chalking topcoat with good gloss and colour retention
- Used as a semi-gloss topcoat for epoxy systems exposed to weathering steelwork
- For industrial and professional use only
Product customisation
Don't forget to save your customization to be able to add to cartTikkurila Temathane PC 50 is a high-solids two-component, semi-gloss polyurethane paint, hardener aliphatic isocyanate, used as a semi-gloss topcoat for epoxy systems exposed to weathering.
Temathane PC 50 forms an easy-to-clean and non-chalking topcoat with good gloss and colour retention, and is an excellent choice when a high-solids topcoat with extremely good gloss and colour retention is required.
Prequalified in the NORSOK system 1 and therefore an excellent choice for the most demanding application areas such as offshore environments, refineries, power plants and bridges
For industrial and professional use only.
Quick Links - Click To Jump To Section:
- Features & Benefits
- Technical Data
- Mixing Ratio
- Recommended Film Thicknesses & Theoretical Coverage
- Drying Times
- Surface Preparation
- Recommended Topcoats
- Application Conditions
- Application
- Mixing Components
- Thinner
- Cleaner
Features & Benefits
- Huge colour range available, with RAL, BS & NCS shades
- Excellent choice when a high-solids topcoat with extremely good gloss and colour retention is required
- Prequalified in the NORSOK system 1 and therefore an excellent choice for the most demanding application areas such as offshore environments, refineries, power plants and bridges
- Excellent weather and abrasion resistance
- Forms easy-to-clean and non-chalking topcoat with good gloss and colour retention
- Used as a semi-gloss topcoat for epoxy systems exposed to weathering
- Recommended for painting of storage tank exteriors, steel buildings and other steelwork
- For industrial and professional use only
Technical Data
Volume solids
- 65±2% (ISO 3233)
Weight solids
- 76±2%
Specific gravity
- 1.3 ± 0.1 kg / l (mixed)
VOC
- The Volatile Organic Compounds amount (ISO 11890) is 330 g/litre of paint mixture.
- VOC content of the paint mixture (thinned 15 % by volume) is 410 g/l.
Pot Life (23℃):
- 1½ hours
Mixing Ratio
Base (Temathane PC 50):
- 5 parts by volume
Hardener (008 7590):
- 1 part by volume
Recommended Film Thicknesses & Theoretical Coverage
Recommended film thicknesses | Theoretical coverage | |
---|---|---|
Wet | Dry | |
125µm | 80µm | 8.1m²/l |
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Drying Times
DFT 80µm | 5℃ | 10℃ | 23℃ | 35℃ |
---|---|---|---|---|
Dust dry, after | 2 hours | 1hour 15 minutes | 1 hour | 20 minutes |
Touch dry, after | 10 hours | 8 hours | 6 hours | 3½ hours |
Recoatable, after | No limitations |
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Surface Preparation
Primed surfaces:
- Oil, grease, salt and dirt are removed from the surface by appropriate means.
- Repair any damage to the primer coat.
- Note the overcoating time of primer. (ISO 12944-4)
Recommended Primers
- Temacoat GPL-S Primer
- Temacoat GPL-S MIO
- Temacoat GF Primer
- Temacoat RM 40
- Temacoat Primer
- Temacoat SPA Primer
- Temabond ST 200
- Temabond ST 300
- Temadur 20
- Temaprime GF
- Temadur 10
Recommended Topcoats
Application Conditions
- All surfaces must be clean, dry and free from contamination.
- The temperature of the ambient air, surface and paint should not fall below 5℃ during application and drying.
- Relative humidity of the air should not exceed 80% during application and drying.
- The surface temperature of steel should remain at least 3°C above the dew point.
- Good ventilation and sufficient air movement is required in confined areas during application and drying.
Mixing Components
- First stir base and hardener separately.
- The correct proportions of base and hardener must be mixed thoroughly before use.
- Use power mixer for mixing.
- Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface and weaken the properties of the coating.
Application
In order to obtain an even, non-porous finish, spray a misty coat: first a thin layer, then let the solvents evaporate for 5–30 minutes and then apply the full coat.
For airless spraying:
- The product is thinned depending on the temperature of the components (base, hardener, thinner) approximately 0–15%.
- Recommended nozzle tip is 0.011"–0.013" and pressure 120–160 bar.
- Spray angle shall be chosen according to the shape of the object.
For conventional spraying:
- The product is thinned depending on the temperature of the components (base, hardener, thinner) approximately 5–15%.
- Recommended nozzle tip is 1.6–1.8 mm and pressure 3–4 bar.
Thinners
- Thinner 1048, Thinner 1067, Thinner 1061
- Thinner 1061 is also suitable for conventional spraying.
Cleaning of Equipment
Data sheet
- Manufacturer
- Tikkurila
- Interior / Exterior Use
- Exterior Use
- For Use On
- Steel
- Application Method
- Spray
- Sheen
- Semi-Gloss
- Colour
- Standard / Ready Mixed
- Single, Two or Three Pack
- Two-Pack
- Pack Size
- 10L
- Parts
- 2
- Base Type
- Polyurethane
- Interior/Exterior Use
- Exterior
- Solvent
- Mixture - see safety sheet
- Mixing Ratio
- 5:1
- Suitable Substrates
- Steel
- Key Features
- Prequalified in the NORSOK system 1 and therefore an excellent choice for the most demanding application areas such as offshore environments, refineries, power plants and bridges
- Touch Dry (at 20°C)
- 6 hours
- Coverage
- 8.1m²/l
- Recommended Thinner/Cleaner
- Thinner 1048, Thinner 1067, Thinner 1061
- Unit Contents
- Base, hardener
- Compatible Primers
- Temacoat GPL-S Primer, Temacoat GPL-S MIO, Temacoat GF Primer & more - see data sheets
- Compatible Topcoats
- Temathane PC 50, Temathane PC 80, Temadur Clear
- Min. Application Temperature
- The temperature of the ambient air, surface and paint should not fall below 5℃ during application and drying.
- Solids by Volume
- 65±2% (ISO 3233)
- VOC
- The Volatile Organic Compounds amount (ISO 11890) is 330 g/litre of paint mixture. VOC content of the paint mixture (thinned 15 % by volume) is 410 g/l.
- Finish
- Semi-gloss
- Size
- 10 litre
- Recommended Dry Film Thickness
- 80µm
- Recommended Wet Film Thickness
- 125µm
- UN Number (Activator)
- UN1263
- UN Number (Base)
- UN1263
- Dry to Recoat (at 23°C)
- 6h
- Dry for Topcoat (at 23°C)
- No limitations.
- Pot Life
- 1½ hours (23℃)
- Specific Gravity
- 1.3 ± 0.1 kg / l (mixed)
- Solids by Weight
- 76±2%
- Base Type
- Solvent-Based
- Suitable For Use On
- Steel
- Suitable For Use On
- Primed Surfaces
- Finish
- Semi-Gloss
- Application Method
- Spray
- Usages
- Colour Retention
- Usages
- Weather Resistance
- Usages
- Non-Chalking
- Usages
- High Solids
- Usages
- Abrasion Resistant
- Usages
- Atmospheric
- Usages
- Gloss Retention
- Product Usage Type
- Topcoat
- Product Range
- Temathane
- Colour Family
- Black
- Colour Family
- White
- Colour Family
- Anthracite Grey
- Colour Family
- Beige
- Colour Family
- Grey
- Colour Family
- Green
- Colour Family
- Blue
- Colour Family
- Red
- Colour Family
- Brown
- Colour Family
- Pink
- Colour Family
- Orange
- Colour Family
- Purple
- Colour Family
- Yellow
- Environment
- Atmospheric
- Touch Dry/Dust Free (@ 20-25°C)
- 6 hours
- Product Attributes
- Gloss Retention
- Product Attributes
- Colour Retention
- Product Attributes
- Easy to Clean
- Product Attributes
- Tough / Durable
- Product Attributes
- Non-Chalking
- Resistance to
- Abrasion
- Resistance to
- Weather
Questions
Question about the product
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
Tikkurila Temathane PC 50 is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT
Tikkurila Temabond ST 200
2 component high-solids, aluminium pigmented modified epoxy maintenance paint for demanding surfaces such as steel structures, railway vehicles, and infastructure in energy and telecommunications. Surface-tolerant high-solids epoxy paint. Very good adhesion even to hand-prepared steel. Lower VOC emissions than conventional epoxy paints....
Tikkurila Temabond ST 300
Tikkurila Temabond ST 300 is a two-component high-solids, modified tintable epoxy maintenance paint for demanding surfaces, and is recommended for repairing of damages caused by transport or installation. Surface-tolerant with a wide colour range For steel and concrete surfaces Very good adhesion, even to hand-prepared steel Lower VOC...
Tikkurila Temacoat GF Primer
Tikkurila Temacoat GF Primer is a two component, polyamide cured epoxy primer containing zinc phosphate that is used as a primer for steel, zinc and aluminium surfaces. For industrial and professional use only For use in epoxy and polyurethane systems For use where high requirements for appearance are set Recommended for agricultural...
Tikkurila Temacoat GPL-S MIO
Tikkurila Temacoat GPL-S MIO is a two-component, polyamide cured epoxy paint pigmented with micaceous iron oxide, with superior adhesion to steel surfaces forming a very strong and durable film that can be used as a primer or an intermediate coat in aggressive environments Fast cure and low-temperature cure hardeners available - click to...
Tikkurila Temacoat GPL-S Primer
Tikkurila Temacoat GPL-S Primer is a two-component, polyamide-cured high build epoxy primer containing zinc phosphate. Excellent adhesion to steel, zinc and aluminium surfaces. Used as a primer or an intermediate coat in paint systems exposed to abrasion and chemical stress. Can be overcoated after a prolonged period of time. Faster...
Tikkurila Temacoat Primer
A two-component resin modified epoxy paint containing anti-corrosive pigments that can be applied at sub-zero temperatures as a primer or an intermediate coat on surfaces exposed to climatic, mechanical and chemical stress. Recommended for building frameworks, tubular bridges, conveyors and other steelwork and equipment Adheres well to...
Tikkurila Temacoat RM 40
2-component, resin modified epoxy primer/topcoat with 4,000+ colours that can be used as a single-coat system. Good adhesion to steel, zinc and aluminium surfaces exposed to severe abrasion or chemical stress. Suitable for concrete surfaces and has a CE marking. Can be used on steel structures in wet environments, e.g. inside pontoons,...
Tikkurila Temacoat SPA Primer
Tikkurila Temacoat SPA Primer, a two-component resin modified epoxy primer with anti-corrosive pigments with excellent adhesion to steel, zinc and aluminium surfaces, that can be applied in thick layers, thus enabling faster production. Has high solids content Used as a primer or an intermediate coat in paint systems exposed to abrasion...
Tikkurila Temadur 10
Tikkurila Temadur 10, a two-component matt polyurethane paint containing anti-corrosive pigments used as a single-coat paint for steel, zinc and aluminium surfaces. Huge colour range available with RAL, BS & NCS shades Can also used as a primer or a matt topcoat in epoxy systems exposed to weathering and/or chemical stress...
Tikkurila Temadur 20
2-pack semi-matt polyurethane paint with 3,800+ colours that can be used as a single-coat paint for steel, zinc and aluminium surfaces with its anti-corrosion pigmentation, and also used as a primer or as a semi-matt topcoat in epoxy-polyurethane systems. It is also suitable for use on uPVC. Resistance to weathering and abrasion MED...