These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3). Please click here for important information about these kits. Kit Contents: SET 1 (Hand Tools) 1 x Rust-Oleum...
Sherwin-Williams Epidek M153
Sherwin-Williams M153 is an aggregate dressed, ultra heavy duty, hard wearing, coal tar free, solvent-less epoxy anti-slip deck coating. It is used for the treatment of deck surfaces subject to the most extreme of operational conditions requiring a high degree of impact and abrasion resistance, where a high level of anti-slip properties need to be retained under conditions of severe crude oil and hydrocarbon contamination.
- Epoxy anti-slip deck coating
- For the treatment of deck surfaces subject to the most extreme of operational conditions
- Complies with NORSOK M501 (Rev.5) System 4
- Two component
- Please note: Also available in Light Grey and Bright Yellow subject to a minimum order quantity of 200L and an extended lead time of up to 14 working days - Please see Sherwin-Williams M153 - Special Colours
Please note: Colours shown are for illustrative purposes only
Sherwin-Williams M153 is an aggregate dressed, ultra heavy duty, hard wearing, coal tar free, solvent-less epoxy anti-slip deck coating. It is used for the treatment of deck surfaces subject to the most extreme of operational conditions requiring a high degree of impact and abrasion resistance, and where a high level of anti-slip properties need to be retained under conditions of severe crude oil and hydrocarbon contamination.
Complies with NORSOK M501 (Rev.5) System 4
- Macropoxy C425V2 Zinc Phosphate Primer/Buildcoat
- Macropoxy L425 Zinc Phosphate Primer
- Macropoxy M262 Hi-Build Finish
Application Conditions & Overcoating
It is preferred that whenever practical Epidek M153 should be applied directly on to blast cleaned steel to Sa21⁄2. M153 may be applied over an approved high build epoxy primer.
If applied over Macropoxy Blast Primer the primer thickness must be carefully controlled. The target DFT is 25μm but the maximum DFT applied must not exceed 40μm. If a high build primer is required please use one of those recommended on the front of this data sheet.
This material should preferably be applied at temperatures in excess of 10°C. In conditions of high relative humidity, ie 80-85% good ventilation conditions are essential. Substrate temperature shall be at least 3°C above the dew point and always above 0°C.
At application temperatures below 10°C, drying and curing times will be significantly extended, and spraying characteristics may be impaired.
Application at ambient air temperatures below 5°C is not recommended.
If it is desired to overcoat outside the times stated on the data sheet, please seek advice of Technical Team.
A two component package comprising Component ‘A’ and ‘B’
Component A (20 litre pail); Containing 12.6 litres base screed unit comprising epoxy resin base, curing agent and fine silica grit.
Component B (nylon sack); Containing 25kg calcined bauxite aggregate (see below).
Pack Size: 12.6 litre unit when mixed
Mixing Ratio: 1.54 parts base to 1 part additive by volume plus silica grit
Weight: 1.84 kg/litre (may vary with shade).
Shelf Life: 2 years from date of manufacture or ‘Use By’ date where specified.
Drying times, curing times and pot life should be considered as a guide only.
The curing reaction of epoxies commences immediately the two components are mixed, and since the reaction is dependent on temperature, the curing time and pot life will be approximately halved by a 10°C increase in temperature and doubled by a 10°C decrease in temperature.
Calcined Bauxite Aggregate
Four sizes of aggregate are available depending on degree of anti-slip properties required and end use:-
1. Light Aggregate (0.85 - 1.70mm )
2. Medium Aggregate (1.40 - 2.00mm )
3. Heavy Aggregate (1.40 - 2.80mm)
4. Road Aggregate (3.00 - 5.00mm)
N.B. Consumption of aggregate will depending upon screed thickness, efficiency of excess aggregate recovery and recycling. For guidance on quantities of aggregate consult sheet entitled Epigrip M153 Supplementary Information.
If it is felt desirable to overcoat the surface of Epidek M153 Heavy Duty Deck Coating or to mark surfaces with a different colour this may be achieved by the application of a coat of Macropoxy M262 Hi-Build Finish.
Numerical values quoted for physical data may vary slightly from batch to batch.
- Application Method
- Mid Sheen
- Standard / Ready Mixed
- VOC Levels
- Ultra-Low (5-49 g/l)
- Single, Two or Three Pack
- Product Certifications
- NORSOK M501 (Rev.5) System 4
- Pack Size
- 0.32m² per litre
- Touch Dry
- 5 Hours
- UN Number (Activator)
- UN Number (Base)
Be the first to ask a question about this product!