• Sherwin-Williams Epigrip C400W

Sherwin-Williams Macropoxy C400W

C400W

We no longer stock this product, but can recommend Sherwin Williams Fast-Clad 7220 as a great alternative.

Quantity

Description

Sherwin-Williams Macropoxy C400W (formerly known as Epigrip C400W) is a multi-functional epoxy zinc phosphate coating specified for use as a primer on blast cleaned structural steel for internal and external environments. Sherwin-Williams Macropoxy C400W may also be used as a high build intermediate coat as well as the final coat where a low sheen industrial and functional finish is required (not for immersion service).

Recommended Use

Specified for use as a primer for structural steel on blast cleaned steel for internal and external environments, it may also be used as a high build intermediate coat as well as the final coat where a low sheen industrial and functional finish is required.

Not for immersion service.

Where good colour and gloss retention is required in an external environment, or a full decorative finish is required in an internal environment, one of our topcoats designed specifically for this role should be chosen. A selection of available topcoats is listed in this data sheet under Recommended Topcoats.

C400W may be applied between 75 and 275 microns DFT in one coat depending on specification requirement. 

Recommended Topcoats

Indefinitely overcoatable with epoxy systems provided the surfaces to be coated have been suitably cleaned. Where a high degree of gloss and colour retention is required overcoat with Acrolon C137V2, Acrolon C237, Acrolon 1850 and Acrolon 7300 within 7 days at a minimum dft of 50 microns or in the case of Acrolon C750V2 overcoat within 4 days. These overcoating times refer to achievement of optimum adhesion @ 23°C and will vary with temperature.

Application Conditions & Overcoating

This material should preferably be applied at temperatures in excess of 5oC. Relative humidity should not exceed 90% and in these conditions good ventilation is essential.

Substrate temperature shall be at least 3oC above the dew point and always above 0°C.

In order to achieve optimum water and chemical resistance, temperature needs to be maintained above 5oC during curing.

It is your responsibility to read the Product Data Sheets (available below) before you place an order and prior to application of the product. The content of this website is our best recommendation and is not advice. Coverage rates quoted are approximate, you agree that coverage depends on the condition of the substrate, surface absorption, texture and application method. We ALWAYS recommend a trial area is coated to ensure the product meets your requirements before use.

Product Details
C400W

Data sheet

Manufacturer
Sherwin-Williams
Water / Solvent Based
Solvent
For Use On
Steel
Application Method
Airless Spray, Spray, Brush, Roller
Sheen
Matt
Colour
Standard / Ready Mixed
Single, Two or Three Pack
Two-Pack
Pack Size
5L, 20L
Coverage
9.2m² per litre
Touch Dry
45 mins
UN Number (Activator)
UN3469
UN Number (Base)
UN1263
Attachments
Download


Customer agrees that before placing an Order, Customer has read and understood the most up to date Product Data Sheet for the Product. Where we have access to the Product Data Sheet from the manufacturer, we will either provide a copy on request, or include a link to the Product Data Sheet available on the manufacturer’s website. Customer further agrees that we have no liability for any errors or omissions contained within the Product Data Sheets. For more information, please see our Terms & Conditions of Sale.


questions keith watson on 2020-04-09 08:41:09
Question: 

Please can you confirm the likely thickness of paint if applied with brush/roller. Thanks

Answer: 

Practical application rates for brush in microns are dry - 65 wet - 94.