PPG SigmaCover 690 is a two-component high solids aluminium pigmented polyamine cured modified epoxy primer/coating designed for maintenance. SigmaCover 690 is a self-priming coating, tolerant to lower grades of steel preparation, and is compatible with most aged, good adhering coatings. It can be recoated with epoxy and polyurethane paints, curing at temperatures down to 5°C (41°F) with low VOC.
Good flow properties
Good impact and abrasion resistance
If the substrate temperature drops below 5°C (41°F) until 0°C (32°F), the wintergrade type should be used (see 7414WG)
No induction time - 3 hours pot life - Touch dry in 4 hours - Fully cured after 5 days
See below for more information on surface preparation, application details and curing times
PPG SigmaCover 690, a two-component high solids aluminium pigmented polyamine cured modified epoxy primer/coating designed for maintenance. The self-priming coating is tolerant to lower grades of steel preparation and is compatible with most aged, good adhering coatings.
SigmaCover 690 can be recoated with epoxy and polyurethane paints, curing at temperatures down to 5°C (41°F) with low VOC. Refer further below for more information on surface preparation, application details and curing times.
Features & Benefits
Two-component high solids aluminium pigmented polyamine cured modified epoxy primer/coating
Primer/coating designed for maintenance
For steel in atmospheric exposure conditions and immersion
Low VOC
Good flow properties
Self-priming coating tolerant to lower grades of steel preparation
Compatible with most aged, good adhering coatings
Good recoatability with epoxy and polyurethane paints
Good curing at temperatures down to 5°C (41°F)
Good impact and abrasion resistance
If the substrate temperature drops below 5°C (41°F) until 0°C (32°F), the wintergrade type should be used (see 7414WG)
No induction time
3 hours pot life
Touch dry in 4 hours
Fully cured after 5 days
See below for more information on surface preparation, application details and curing times
Reference
Colour
Size
Gloss Level
328960
Aluminium (light)
4 litres
Semi-gloss
-
Aluminium (light)
20 litres
Semi-gloss
328960
Aluminium (dark)
4 litres
Semi-gloss
-
Aluminium (dark)
20 litres
Semi-gloss
Product Data
Two-component high solids aluminium pigmented polyamine cured modified epoxy primer/coating
Hardener: at least 24 months when stored cool and dry
Notes:
See below for more information on surface preparation, application details and curing times
Surface Preparation
Recommended Substrate Conditions and Temperatures
Atmospheric exposure conditions
Steel;
Blast cleaned to ISO-Sa2 or power tool cleaned to ISO-St2 for good corrosion protection
Steel with approved shop primer;
Sweep blasted to SPSS-Ss or power tool cleaned to SPSS-Pt2
Existing sound coating systems;
sufficiently roughened, dry and cleaned
Immersion in water
Steel;
Blast cleaned to ISO-Sa2½
Steel with approved zinc silicate shop primer;
sweep Blasted to SPSS-Ss or power tool cleaned to SPSS-Pt3
Substrate Temperature & Application Conditions
Substrate temperature during application and curing should be above 5°C (41°F)
Substrate temperature during application and curing should be at least 3°C (5°F) above dew point
Application
Instructions for Use
Mixing ratio by volume: base to hardener 77.5:22:5
The temperature of the mixed base and hardener should preferably be above 15°C (59°F), otherwise extra thinner may be required to obtain application viscosity
Adding too much thinner results in reduced sag resistance and slower cure
Thinner should be added after mixing the components
Overcoating interval for DFT up to 125 µm (5.0 mils)
Overcoating with...
Interval
5°C (41°F)
10°C (50°F)
15°C (59°F)
20°C (68°F)
30°C (86°F)
40°C (104°F)
Itself
Minimum
48 hours
36 hours
20 hours
12 hours
8 hours
6 hours
Maximum
6 months
6 months
6 months
4 months
3 months
3 months
Note:
Surface should be dry and free from any contamination
For polyurethane paints the minimum overcoating time should be raised with 50%
Curing time for DFT up to 125 µm (5.0 mils)
Substrate temperature
Dry to touch
Dry to handle
Full Cure
5°C (41°F)
16 hours
48 hours
10 days
10°C (50°F)
9 hours
36 hours
7 days
15°C (59°F)
6 hours
20 hours
6 days
20°C (68°F)
4 hours
12 hours
5 days
30°C (86°F)
3 hours
8 hours
4 days
40°C (104°F)
2 hours
6 hours
48 hours
Notes:
Adequate ventilation must be maintained during application and curing (please refer to information sheets 1433 and (1434)
Pot Life (at application viscosity)
Mixed product temperature
Pot life
15°C (59°F)
5 hours
20°C (68°F)
3 hours
30°C (86°F)
2 hours
40°C (104°F)
1 hours
50°C (122°F)
1 hours
Safety Precautions
For paint and recommended thinners, see information sheets information sheet 1430, information sheet 1431 and the relevant Material Safety Data Sheets in the attachments section above
This is a solvent-borne paint and care should be taken to avoid inhalation of spray mist or vapor, as well as contact between the wet paint and exposed skin or eyes
Customer agrees that before placing an Order, Customer has read and understood the most up to date Product Data Sheet for the Product. Where we have access to the Product Data Sheet from the manufacturer, we will either provide a copy on request, or include a link to the Product Data Sheet available on the manufacturer’s website. Customer further agrees that we have no liability for any errors or omissions contained within the Product Data Sheets. For more information, please see our Terms & Conditions of Sale.
PPG SigmaCover 690 is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3). Please click here for important information about these kits. Kit Contents: SET 1 (Hand Tools)1 x Rust-Oleum...