Tikkurila Temabond WG 200 is two-component, low temperature curing, aluminium pigmented high-solids modified epoxy metal paint.
Good chemical, solvent and abrasion resistance, due to the aluminium pigments
Especially used as a primer for steel surfaces difficult to clean in process and chemical industry and in water immersion
Excellent adhesion to blast cleaned or hand prepared steel
Recommended for repainting and touch-up painting of bridges, cisterns and different types of steelwork and equipment in wood-processing and chemical industry, such as paper machines, conveyors, tubular bridges etc
Tikkurila Temabond WG 200 is a winter grade low temperature curing, semi gloss high-solids modified epoxy paint.
Temabond WG 200 has good chemical, solvent and abrasion resistance, due to the aluminium pigments. Especially used as a primer for steel surfaces difficult to clean in process and chemical industry and in water immersion.
It has excellent adhesion to blast cleaned or hand prepared steel, and has a low solvent content; lower solvent emissions than with traditional epoxy paints.
Please note this is a special order item with an approximate lead time of 1 - 2 weeks. Please contact Rawlins Paints' Technical Support Team on0113 2455450(option 2) or send a message to[email protected]for more information.
Good chemical, solvent and abrasion resistance, due to the aluminium pigments.
Especially used as a primer for steel surfaces difficult to clean in process and chemical industry and in water immersion.
Excellent adhesion to blast cleaned or hand prepared steel.
High film build properties, also by brush.
Recommended for repairing of damages caused by transport or installation.
Low solvent content - lower solvent emissions than with traditional epoxy paints.
Can also be applied on old alkyd paint surfaces and as a single coat paint.
Recommended for repainting and touch-up painting of bridges, cisterns and different types of steelwork and equipment in wood-processing and chemical industry, such as paper machines, conveyors, tubular bridges etc.
Technical Data
Volume Solids: 80±2% (ISO 3233).
Weight Solids: 83±2%.
Specific Gravity: 1.3 kg / l (mixed).
Mixing Ratio:
Base - 1 part by volume - Temabond WG 200. .
Hardener - 1 part by volume - 008 7519.
Pot Life (23°C): 1½ hours.
Recommended Film Thicknesses and Theoretical Coverage:
Recommended film thicknesses
Theoretical coverage
Wet
Dry
125µm
100µm
8.0 m²/l
250µm
200µm
4.0 m²/l
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Drying Time:
DFT 150µm
-5°C
0°C
5°C
10°C
23°C
Dust dry, after
18h
14h
6h
3h
2h
Touch dry, after
48h
36h
17h
9h
5h
Recoatable, min after
48h
36h
17h
9h
5h
Recoatable without sanding, max. after
2 months
2 months
2 months
1 month
14d
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Gloss: Semi-gloss.
Colour Shades: Aluminium. The colour will change in outdoor use.
Surface Preparation
Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4).
Steel surfaces:
Remove rust by tool cleaning to minimum St2 or blast clean to Sa2 or Sa2½. Blast clean to grade Sa2½ for immersion. (ISO 8501-1).
Previously Painted Surfaces:
Roughen old paint surfaces using e.g. abrasive wheel, sand paper or blast cleaning.
All surfaces must be clean, dry and free from contamination.
The temperature of the ambient air and the surface should not fall below -5ºC during application and drying.
The temperature of the paint should be at least +15ºC.
Relative humidity of the air should not exceed 80% during application and drying.
The surface temperature of steel should remain at least 3°C above the dew point.
Good ventilation and sufficient air movement is required in confined areas during application and drying.
Note! There is a natural tendency of this coating to chalk, discolor or yellow unevenly. It is recommended to use polyurethane topcoat when there are high aesthetic requirements on colour appearance.
Mixing Components
First stir base and hardener separately.
The correct proportions of base and hardener must be mixed thoroughly before use.
Use power mixer for mixing.
Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface and weaken the properties of the coating.
Application
For airless spraying:
The product is thinned depending on the temperature of the components 0–10%.
Recommended nozzle tip is 0.013"–0.019" and pressure 120–180 bar.
Spray angle shall be chosen according to the shape of the object.
For brush application the product should be thinned according to the circumstances.
Customer agrees that before placing an Order, Customer has read and understood the most up to date Product Data Sheet for the Product. Where we have access to the Product Data Sheet from the manufacturer, we will either provide a copy on request, or include a link to the Product Data Sheet available on the manufacturer’s website. Customer further agrees that we have no liability for any errors or omissions contained within the Product Data Sheets. For more information, please see our Terms & Conditions of Sale.
Tikkurila Temabond WG 200 is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
Tikkurila Temabond ST 300 is a two-component high-solids, modified tintable epoxy maintenance paint for demanding surfaces, and is recommended for repairing of damages caused by transport or installation.Surface-tolerant with a wide colour range For steel and concrete surfaces Very good adhesion, even to hand-prepared steel Lower VOC...
Tikkurila Temacoat GPL-S MIO is a two-component, polyamide cured epoxy paint pigmented with micaceous iron oxide, with superior adhesion to steel surfaces forming a very strong and durable film that can be used as a primer or an intermediate coat in aggressive environmentsFast cure and low-temperature cure hardeners available - click to...
Tikkurila Temacoat GPL-S Primer is a two-component, polyamide-cured high build epoxy primer containing zinc phosphate.Excellent adhesion to steel, zinc and aluminium surfaces. Used as a primer or an intermediate coat in paint systems exposed to abrasion and chemical stress. Can be overcoated after a prolonged period of time. Faster...
Temacoat GPL, a two-component, amine adduct cured mar and chemical resistant epoxy topcoat used especially as a finishing coat especially for objects exposed to heavy abrasion and chemical attack. Due to CE marking it is also suitable for concrete surfaces in process industries.Recommended for bridges, tanks and different types of...
Tikkurila Temacoat RM 40, a two-component, resin modified epoxy primer/topcoat that can be used as a single-coat system.Good adhesion to steel, zinc and aluminium surfaces exposed to severe abrasion or chemical stress Suitable for concrete surfaces and has a CE marking Can be used on steel structures in wet environments, e.g. inside...
Tikkurila Temacryl EA 50, a two-component, semi-gloss, non-isocyanate acrylic finish recommended for use as a semigloss topcoat for epoxy systems exposed to weathering and/or chemical stress.Huge colour range - RAL, BS & NCS shades available Excellent weathering and abrasion resistance A durable, non-chalking and easy-to-clean...
Tikkurila Temadur 10, a two-component matt polyurethane paint containing anti-corrosive pigments used as a single-coat paint for steel, zinc and aluminium surfaces.Huge colour range available with RAL, BS & NCS shades Can also used as a primer or a matt topcoat in epoxy systems exposed to weathering and/or chemical stress...
2-pack semi-matt polyurethane paint with 3,800+ colours that can be used as a single-coat paint for steel, zinc and aluminium surfaces with its anti-corrosion pigmentation, and also used as a primer or as a semi-matt topcoat in epoxy-polyurethane systems. It is also suitable for use on uPVC.Resistance to weathering and abrasion MED...
Tikkurila Temadur 50, a time-proven, easy-to-use general purpose topcoat for constructional steelwork and machinery, with a wide range of colours to choose from.Two-component, durable and non-chalking semi-gloss polyurethane paint, hardener aliphatic isocyanate Forms a durable, easy-to-clean and non-chalking topcoat with good gloss and...
Tikkurila Temadur 90, 2-pack, high gloss polyurethane paint recommended to be used as a glossy decorative finishing coat for epoxy systems on a variety of substrates such as steel, aluminium, concrete etc. exposed to severe weathering and/or chemical stress.Forms a durable, easy-to-clean and non-chalking topcoat with outstanding gloss and...
Tikkurila Temaline TL is a two-component, solvent free epoxy coating.Very high sag resistance, which enables achieving a thick paint film with one application. The product is an excellent choice for tanks and reservoirs storing many kinds of fuels like gasoline, diesel, kerosene and lead-free gasoline. Intended for use as a heavy-duty...
Tikkurila Temathane PC 50, a high-solids two-component, semi-gloss polyurethane paint, hardener aliphatic isocyanate recommended for painting of storage tank exteriors, steel buildings and other steelwork.Huge colour range available, with RAL, BS & NCS shades Prequalified in the NORSOK system 1 and therefore an excellent choice for...
Tikkurila Temathane PC 80, a high-solids two-component, glossy polyurethane paint (with hardener aliphatic isocyanate) that is particularly suitable for harsh environments, helping extend the service life of the paint system.Huge colour range with RAL, BS & NCS shades Excellent choice when a high-solids topcoat with extremely good...
Tikkurila Temathane 50 is a two-component, semi-gloss polyurethane paint, hardener aliphatic isocyanate.Dries rapidly and is easy to apply. Recommended to be used as a semi-gloss topcoat for epoxy and polyurethane systems exposed to weathering. A durable, easy to clean and non-chalking topcoat. Excellent weathering and abrasion...
Tikkurila Temathane 90 is a two-component, glossy polyurethane paint, hardener aliphatic isocyanate.The paint is used as a glossy topcoat for epoxy and polyurethane systems exposed to weathering. Forms a durable, easy-to-clean and non-chalking finish. Suitable for painting the outside of storage tanks, steel building and other steelwork....
These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3). Please click here for important information about these kits. Kit Contents: SET 1 (Hand Tools)1 x Rust-Oleum...