Tikkurila Temabond ST 200 is a two component high-solids, aluminium pigmented modified epoxy maintenance paint for demanding surfaces. An ideal solution for maintenance painting due to its very good adhesion even to hand-prepared steel. As a high-solids product, the paint has lower VOC emissions than conventional epoxy paints.

Temabond ST 200 withstands immersion in water and can therefore be used on steel structures immersed in water or buried in soil.

Due to its aluminium pigmentation, Temabond ST 200 forms a very tight film with good chemical and abrasion resistance. The paint is used in systems for repainting and touch-up painting steel surfaces that are difficult to clean, such as bridges, cisterns and different types of steelwork and equipment in the wood-processing and chemical industries.

Temabond ST 200 mastic paint has the ability to penetrate rust and adhere to the underlying steel surface, effectively preventing further corrosion. A barrier pigmented Temabond epoxy paint protects against moisture and oxygen, preventing their corrosive effect on steel.

Quick Links - Click To Jump To Section:

• Features & Benefits
• Technical Data
• Surface Preparation
• Recommended Primers
• Recommended Topcoats
• Application Conditions
• Mixing Components
• Application
• Thinner/Cleaning
• VOC
• Health And Safety

Features & Benefits

• Due to the aluminium pigmentation forms a very tight coat with good chemical and abrasion resistance.
• Used in systems for repainting and touch-up painting of steel surfaces which are difficult to clean such as bridges, cisterns and different types of steelwork and equipment in the wood-processing and chemical industry.
• An ideal solution for maintenance painting due to very good adhesion even to hand prepared steel.
• As a high-solids product Temabond ST 200 has lower VOC emissions than traditional epoxy paints.
• Resists immersion in water and can therefore be used e.g. in steel structures in water and soil immersion.
• High film build properties, also by brush.
• Can also be applied on old alkyd paint surfaces.
• Can be used as a single coat paint.
• Winter grade version Temabond WG 200 can be cured at lower temperatures.
• Recommended for repairing of damages caused by transport or installation.

Technical Data

• Volume Solids: 80±2% (ISO 3233)
• Weight Solids: 87±2%
• Specific Gravity: 1.4 kg / l (mixed)
• Pot Life (23℃): 1½ hours
• Mixing Ratio:
• Base - 1 part by volume - Temabond ST 200
• Hardener - 1 part by volume - 008 7501

Recommended Film Thicknesses and Theoretical Coverage

Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.

Drying Times

Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation

Surface Preparation

Oil, grease, salts and dirt are removed by appropriate means (ISO 12944-4).

Steel Surfaces:

• Remove rust by tool cleaning to minimum St2 or blast clean to Sa2 or Sa2½.
• Blast clean to grade Sa2½ for immersion (ISO 8501-1).

Earlier painted surfaces:

• Roughen old paint surfaces using e.g. abrasive wheel, sand paper or blast cleaning.

Recommended Primers

• Temabond ST 200
• Temazinc 77
• Temazinc 99
• Temacoat SPA Primer
• Temacoat Primer
• Temanyl MS Primer

Recommended Topcoats

• Temacoat GPL
• Temacoat GPL-S MIO
• Temacoat GPL-S Primer
• Temacoat GS 50
• Temacoat RM 40
• Temabond ST 300
• Temacryl EA 50
• Temadur 10
• Temadur 20
• Temadur 50
• Temadur 90
• Temathane 50
• Temathane 90
• Temathane PC 50
• Temathane PC 80
• Temacoat SPA 50
• Temacoat Primer

Application Conditions

• All surfaces must be clean, dry and free from contamination.
• The temperature of the ambient air, surface and paint should not fall below +10ºC during application and drying.
• Relative humidity of the air should not exceed 80% during application and drying.
• The surface temperature of steel should remain at least 3°C above the dew point.
• Good ventilation and sufficient air movement is required in confined areas during application and drying.

Note! There is a natural tendency of this coating to chalk, discolor or yellow unevenly. It is recommended to use polyurethane topcoat when there are high aesthetical requirements on colour appearance.

Mixing Components

• First stir base and hardener separately.
• The correct proportions of base and hardener must be mixed thoroughly before use.
• Use power mixer for mixing.
• Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface and weaken the properties of the coating.

Application

• For airless spraying, the product is thinned approximately 0–10%.
• Recommended nozzle tip is 0.013"–0.019" and pressure 140–180 bar.
• Spray angle shall be chosen according to the shape of the object.
• For brush application product should be thinned according to the circumstances.

Thinner/Cleaning

Thinner

Thinner 1031.

Cleaning Of Equipment

Thinner 1031.

VOC

The Volatile Organic Compounds amount is 200 g/litre of paint mixture. VOC content of paint mixture (thinned 10 % by volume) is 260 g/l.

Health And Safety

Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets.

For industrial and professional use only.

Please contact Rawlins Paints' Technical Support Team on 0113 2455450 (option 2) or send a message to [email protected] for more information.